- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 11.0
- 弯曲强度 [MPa]: 11.7
- 弯曲模量 [MPa]: 0.317
- 热变形温度 [℃]: 49.0
- 脆化温度 [℃]: -71.0
- 透光率 [%]: 90.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.924 - 0.945 g/cc | 0.0334 - 0.0341 lb/in³ | Average value: 0.937 g/cc Grade Count:65 |
Environmental Stress Crack Resistance | 10.0 - 1000 hour | 10.0 - 1000 hour | Average value: 334 hour Grade Count:23 |
>= 1000 hour @Temperature 50.0 - 50.0 °C | >= 1000 hour @Temperature 122 - 122 °F | Average value: 1000 hour Grade Count:1 | |
Melt Flow | 2.00 - 50.0 g/10 min | 2.00 - 50.0 g/10 min | Average value: 6.34 g/10 min Grade Count:65 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 50.0 - 67.0 | 50.0 - 67.0 | Average value: 56.6 Grade Count:55 |
Tensile Strength, Ultimate | 11.7 - 27.1 MPa | 1700 - 3930 psi | Average value: 19.5 MPa Grade Count:10 |
Tensile Strength, Yield | 11.0 - 22.0 MPa | 1600 - 3190 psi | Average value: 18.1 MPa Grade Count:64 |
Elongation at Break | 150 - 1000 % | 150 - 1000 % | Average value: 563 % Grade Count:64 |
Elongation at Yield | 10.0 - 12.0 % | 10.0 - 12.0 % | Average value: 11.1 % Grade Count:6 |
Flexural Modulus | 0.317 - 0.931 GPa | 46.0 - 135 ksi | Average value: 0.629 GPa Grade Count:65 |
Dart drop Total Energy | 200 - 220 J/cm | 0.375 - 0.412 ft-lb/mil | Average value: 208 J/cm Grade Count:4 |
Thermal Properties | Metric | English | Comments |
Melting Point | 125 - 128 °C | 257 - 262 °F | Average value: 126 °C Grade Count:11 |
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 60.0 °C | 120 - 140 °F | Average value: 55.1 °C Grade Count:11 |
Deflection Temperature at 1.8 MPa (264 psi) | 37.0 - 42.0 °C | 98.6 - 108 °F | Average value: 39.1 °C Grade Count:7 |
Vicat Softening Point | 113 - 121 °C | 235 - 250 °F | Average value: 117 °C Grade Count:6 |
Brittleness Temperature | -71.0 - -70.0 °C | -95.8 - -94.0 °F | Average value: -70.2 °C Grade Count:5 |
Optical Properties | Metric | English | Comments |
Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:4 |