- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.935
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ISO 1183 |
| Melt Flow | 0.70 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.70 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| 15 g/10 min @Load 21.6 kg, Temperature 190 °C | 15 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Tensile Modulus | 0.500 GPa | 72.5 ksi | MD; ASTM D882-A |
| 0.650 GPa | 94.3 ksi | TD; ASTM D882-A | |
| Coefficient of Friction | 0.40 | 0.40 | ISO 8295 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ISO 6383/2 |
| Elmendorf Tear Strength TD | 150 g | 150 g | ISO 6383/2 |
| Elmendorf Tear Strength, MD | 2.04 g/micron | 51.8 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 26.5 g/micron | 673 g/mil | ISO 6383/2 |
| Dart drop Test | 220 g @Thickness 0.0250 mm | 0.485 lb @Thickness 0.000984 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ISO 527-3 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 210 °C | 374 - 410 °F | |