- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.937
- 拉伸强度 [MPa]: 19.0
- 弯曲模量 [MPa]: 0.800
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505 |
| Environmental Stress Crack Resistance | 1500 hour | 1500 hour | Condition C (100% Igepal), F50, ASTM D1693; Condition B (10% Igepal), F50: 1500, ASTM D1693 |
| Melt Flow | 12 g/10 min | 12 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 2 in per min; ASTM D638 Type IV |
| Elongation at Break | >= 700 % | >= 700 % | 2 in per min; ASTM D638 Type IV |
| Flexural Modulus | 0.800 GPa | 116 ksi | ASTM D790 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 - 232 °C | 379 - 450 °F | Extrusion |