- 熔体流动速率 [g/10min]: 4.8
- 密度 [g/cm3]: 0.937
- 拉伸强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.804
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ASTM D1505 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 98 | 98 | ASTM D2240 |
| Hardness, Shore D | 57 | 57 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM D638 |
| Flexural Modulus | 0.804 GPa | 117 ksi | ASTM D790 |
| Secant Modulus | 1.805 GPa | 261.8 ksi | 0.01; ASTM D638 |