- 密度 [g/cm3]: 0.928
- 拉伸强度 [MPa]: 13.5
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.928 - 0.930 g/cc | 0.0335 - 0.0336 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 0.25 - 0.35 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.25 - 0.35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
| Tensile Strength, Yield | 13.5 MPa | 1960 psi | ASTM D638 |
| Elongation at Break | 550 % | 550 % | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 °C | 241 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |