- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.931
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Elongation at Break, MD | 744 % | 744 % | ASTM D882 |
| Film Elongation at Break, TD | 980 % | 980 % | ASTM D882 |
| Secant Modulus, MD | 0.380 GPa | 55.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.450 GPa | 65.3 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 3.00 g/micron | 76.2 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Dart Drop | 4.00 g/micron | 102 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.0 MPa | 6380 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.9 % @Thickness 0.0250 mm | 8.9 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 220 °C | 410 - 428 °F | |