- 密度 [g/cm3]: 0.929
- 拉伸强度 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 - 0.933 g/cc | 0.0336 - 0.0337 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 1.8 - 2.6 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 - 2.6 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.0 MPa | 1740 psi | ASTM D638 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 |
| Film Elongation at Break, TD | 675 % | 675 % | ASTM D882 |
| Elongation at Break | 520 % | 520 % | ASTM D638 |
| Secant Modulus, MD | 0.150 GPa | 21.8 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.160 GPa | 23.2 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.65 | 0.65 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 6.60 g/micron | 168 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.50 g/micron | 114 g/mil | ASTM D1922 |
| Dart drop Test | 100 g | 0.221 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 90 % | 90 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 155 - 170 °C | 311 - 338 °F | Plasticizing Zone |
| 165 - 175 °C | 329 - 347 °F | Mixture Zone | |
| Feed Temperature | 145 - 160 °C | 293 - 320 °F | |
| Adapter Temperature | 175 - 190 °C | 347 - 374 °F | |