- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 16.3993
- 弯曲模量 [MPa]: 0.6000
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| Melt Index of Compound | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 9.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength, Yield | 16.3993 MPa | 2378.52 psi | 2"/min; ASTM D638 |
| Elongation at Break | 515 % | 515 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.6000 GPa | 87.02 ksi | ASTM D790 |