- 熔体流动速率 [g/10min]: 6.2
- 密度 [g/cm3]: 0.93
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 6.2 g/10 min | 6.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Dart drop Test | 60.0 g | 0.132 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.3 MPa | 4400 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
| 1% Secant Modulus, MD | 262 MPa | 38000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 296 MPa | 43000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D2457 |