- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.933
- 缺口冲击强度: 1.15
- 拉伸强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.590
- 热变形温度 [℃]: 61.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505-98 |
| Melt Flow | 3.2 - 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.2 - 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 39.0 MPa | 5660 psi | ASTM D638-03 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638-02 |
| Elongation at Break | 880 % | 880 % | ASTM D638-02 |
| Elongation at Yield | 12 % | 12 % | ASTM D638-02 |
| Flexural Modulus | 0.590 GPa | 85.6 ksi | 2% secant; ASTM D790-02 |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256-03 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 61.0 °C | 142 °F | ASTM D648-97 |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525-97 |