- 熔体流动速率 [g/10min]: 0.15
- 弯曲模量 [MPa]: 0.740
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.938 g/cc | 0.938 g/cc | ISO 1183 |
| Melt Flow | 0.15 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.15 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 14 g/10 min @Load 21.6 kg, Temperature 190 °C | 14 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 20.0 MPa @Thickness 0.0400 mm | 2900 psi @Thickness 0.00157 in | ISO 527-3 |
| 21.0 MPa @Thickness 0.0200 mm | 3050 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Tensile Strength at Yield, TD | 20.0 MPa @Thickness 0.0400 mm | 2900 psi @Thickness 0.00157 in | ISO 527-3 |
| 22.0 MPa @Thickness 0.0200 mm | 3190 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Elongation at Break, MD | 420 % @Thickness 0.0200 mm | 420 % @Thickness 0.000787 in | ISO 527-3 |
| 530 % @Thickness 0.0400 mm | 530 % @Thickness 0.00157 in | ISO 527-3 | |
| Film Elongation at Break, TD | 520 % @Thickness 0.0200 mm | 520 % @Thickness 0.000787 in | ISO 527-3 |
| 620 % @Thickness 0.0400 mm | 620 % @Thickness 0.00157 in | ISO 527-3 | |
| Flexural Modulus | 0.740 GPa @Strain <=0.250 % | 107 ksi @Strain <=0.250 % | ISO 178 |
| Elmendorf Tear Strength, MD | 0.900 g/micron @Thickness 0.0200 mm | 22.9 g/mil @Thickness 0.000787 in | ISO 6383-2 |
| 1.70 g/micron @Thickness 0.0400 mm | 43.2 g/mil @Thickness 0.00157 in | ISO 6383-2 | |
| Elmendorf Tear Strength, TD | 13.3 g/micron @Thickness 0.0200 mm | 338 g/mil @Thickness 0.000787 in | ISO 6383-2 |
| 18.9 g/micron @Thickness 0.0400 mm | 480 g/mil @Thickness 0.00157 in | ISO 6383-2 | |
| Dart drop Test | 190 g @Thickness 0.0200 mm | 0.419 lb @Thickness 0.000787 in | ISO 7765-1 |
| 260 g @Thickness 0.0400 mm | 0.573 lb @Thickness 0.00157 in | ISO 7765-1 | |
| Film Tensile Strength at Break, MD | 56.0 MPa @Thickness 0.0400 mm | 8120 psi @Thickness 0.00157 in | ISO 527-3 |
| 69.0 MPa @Thickness 0.0200 mm | 10000 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Tensile Strength at Break, TD | 51.0 MPa @Thickness 0.0200 mm | 7400 psi @Thickness 0.000787 in | ISO 527-3 |
| 52.0 MPa @Thickness 0.0400 mm | 7540 psi @Thickness 0.00157 in | ISO 527-3 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | ISO 11357 |
| Vicat Softening Point | 121 °C | 250 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |