- 熔体流动速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.948
- 缺口冲击强度: 4.0
- 拉伸强度 [MPa]: 17.5
- 弯曲强度 [MPa]: 27.5
- 弯曲模量 [MPa]: 0.580
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | >= 3000 hour | >= 3000 hour | Condition B and C; ASTM D 1693 |
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ASTM D2240 |
| Tensile Strength, Ultimate | 27.5 MPa | 3990 psi | ASTM D638 |
| Tensile Strength, Yield | 17.5 MPa | 2540 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.580 GPa | 84.1 ksi | Tangent-Method 1; ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm | 7.49 ft-lb/in | Partial Break; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |