- 熔体流动速率 [g/10min]: 0.23
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.937 g/cc | 0.937 g/cc | ISO 1183 |
Water Vapor Transmission | 12.4 g/m²/day | 0.800 g/100 in²/day | ASTM E96/66 |
Melt Flow | 0.23 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.23 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
20 g/10 min @Load 21.6 kg, Temperature 190 °C | 20 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
Mechanical Properties | Metric | English | Comments |
Film Tensile Strength at Yield, MD | 12.4 MPa | 1800 psi | ASTM D882, A |
Film Tensile Strength at Yield, TD | 19.3 MPa | 2800 psi | ASTM D882, A |
Film Elongation at Break, MD | 500 % | 500 % | ASTM D882, A |
Film Elongation at Break, TD | 900 % | 900 % | ASTM D882, A |
Elmendorf Tear Strength MD | 18 g | 18 g | ASTM D1922 |
Elmendorf Tear Strength TD | 1350 g | 1350 g | ASTM D1922 |
Dart drop Test | <= 50.0 g | <= 0.110 lb | ASTM D1709,A |
Film Tensile Strength at Break, MD | 57.2 MPa | 8300 psi | ASTM D882, A |
Film Tensile Strength at Break, TD | 36.5 MPa | 5300 psi | ASTM D882, A |
1% Secant Modulus, MD | 441 MPa | 64000 psi | ASTM D882, A |
1% Secant Modulus, TD | 586 MPa | 85000 psi | ASTM D882, A |
Thermal Properties | Metric | English | Comments |
Melting Point | 126 °C | 259 °F | ASTM D3417 |
Processing Properties | Metric | English | Comments |
Melt Temperature | 193 - 216 °C | 380 - 420 °F | Extrusion |