- 熔体流动速率 [g/10min]: 6.0
- 拉伸强度 [MPa]: 18.0
- 弯曲模量 [MPa]: 0.700
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.935 g/cc | 0.935 g/cc | ISO 1183 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133/D |
| 135 g/10 min @Load 21.6 kg, Temperature 190 °C | 135 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ISO 527-2 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-2 |
| Elongation at Break | >= 700 % | >= 700 % | ISO 527-2 |
| Flexural Modulus | 0.700 GPa | 102 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | ISO 11357 |
| Vicat Softening Point | 121 °C | 250 °F | ISO 306 |