- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.005
- 缺口冲击强度: 100.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 0.647
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 - 1.86 g/cc | 0.0574 - 0.0672 lb/in³ | Average value: 1.75 g/cc Grade Count:15 |
| Water Absorption | 0.00500 - 0.100 % | 0.00500 - 0.100 % | Average value: 0.0914 % Grade Count:11 |
| Oxygen Transmission | 70.0 cc-mm/m²-24hr-atm | 178 cc-mil/100 in²-24hr-atm | Average value: 70.0 cc-mm/m²-24hr-atm Grade Count:14 |
| Nitrogen Transmission | 20.0 - 104 cc-mm/m²-24hr-atm | 50.8 - 263 cc-mil/100 in²-24hr-atm | Average value: 32.0 cc-mm/m²-24hr-atm Grade Count:14 |
| Viscosity | 1.00e+6 - 1.00e+7 cP @Temperature 300 - 330 °C | 1.00e+6 - 1.00e+7 cP @Temperature 572 - 626 °F | Average value: 5.50e+6 cP Grade Count:10 |
| Linear Mold Shrinkage | 0.0300 - 0.0400 cm/cm | 0.0300 - 0.0400 in/in | Average value: 0.0350 cm/cm Grade Count:10 |
| Melt Flow | 2.00 - 50.0 g/10 min | 2.00 - 50.0 g/10 min | Average value: 17.8 g/10 min Grade Count:16 |
| Deformation | 2.30 - 5.40 % | 2.30 - 5.40 % | Average value: 3.85 % Grade Count:10 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75.0 | 75.0 | Average value: 75.0 Grade Count:10 |
| Tensile Strength, Ultimate | 35.0 - 50.0 MPa | 5080 - 7250 psi | Average value: 43.8 MPa Grade Count:16 |
| Elongation at Break | 300 - 460 % | 300 - 460 % | Average value: 418 % Grade Count:17 |
| Modulus of Elasticity | 0.490 - 0.827 GPa | 71.1 - 120 ksi | Average value: 0.654 GPa Grade Count:11 |
| Flexural Modulus | 0.647 - 1.37 GPa | 93.8 - 199 ksi | Average value: 1.06 GPa Grade Count:15 |
| Compressive Yield Strength | 11.0 MPa | 1600 psi | Average value: 11.0 MPa Grade Count:10 |
| Izod Impact, Notched | 100 - 5340 J/cm | 187 - 10000 ft-lb/in | Grade Count:4 |
| Izod Impact, Unnotched | NB | NB | Grade Count:10 |
| Coefficient of Friction | 0.0550 - 0.0780 | 0.0550 - 0.0780 | Average value: 0.0665 Grade Count:10 |
| Coefficient of Friction, Static | 0.0600 | 0.0600 | Average value: 0.0600 Grade Count:10 |
| Taber Abrasion, mg/1000 Cycles | 127 - 149 | 127 - 149 | Average value: 141 Grade Count:10 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | Average value: 1.00e+16 ohm-cm Grade Count:10 |
| Dielectric Constant | 2.40 - 2.75 | 2.40 - 2.75 | Average value: 2.58 Grade Count:17 |
| Dielectric Strength | 7.87 - 16.0 kV/mm | 200 - 406 kV/in | Average value: 15.3 kV/mm Grade Count:11 |
| Dissipation Factor | 0.000400 - 0.00820 | 0.000400 - 0.00820 | Average value: 0.00281 Grade Count:16 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 - 131 µm/m-°C | 27.8 - 73.0 µin/in-°F | Average value: 75.6 µm/m-°C Grade Count:11 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | Average value: 0.240 W/m-K Grade Count:10 |
| Melting Point | 160 - 266 °C | 320 - 510 °F | Average value: 233 °C Grade Count:15 |
| Maximum Service Temperature, Air | 150 - 154 °C | 302 - 310 °F | Average value: 150 °C Grade Count:11 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:17 |
| Oxygen Index | 31.0 - 40.0 % | 31.0 - 40.0 % | Average value: 31.5 % Grade Count:17 |