- 密度 [g/cm3]: 1.83
- 缺口冲击强度: 6.15
- 拉伸强度 [MPa]: 27.0
- 弯曲模量 [MPa]: 1.21
- 热变形温度 [℃]: 89.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D 792 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.00 % @Time 86400 sec | 0.00 % @Time 24.0 hour | 50% RH; ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D 638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 |
| 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 53 % | 53 % | Type I, 5 mm/min; ASTM D 638 |
| 78 % | 78 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 22 % | 22 % | 5 mm/min; ISO 527 |
| 23 % | 23 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 1.51 GPa | 219 ksi | 1 mm/min; ISO 527 |
| 1.70 GPa | 247 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 24.0 MPa | 3480 psi | ISO 178 |
| Flexural Modulus | 1.21 GPa | 175 ksi | 2 mm/min; ISO 178 |
| 1.28 GPa | 186 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 6.15 J/cm @Temperature 23.0 °C | 11.5 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 13.4 J/cm @Temperature 23.0 °C | 25.1 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C | 17.6 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 119 kJ/m² @Temperature 23.0 °C | 56.6 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Impact Test | 26.0 J @Temperature 23.0 °C | 19.2 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 44.4 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 48.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 88.0 °C @Thickness 3.20 mm | 190 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 52.0 °C @Thickness 3.20 mm | 126 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |