- 熔体流动速率 [g/10min]: 6.0
- 吸水率 [%]: 0.01
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.655
- 热变形温度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.77 - 1.79 g/cc | 1.77 - 1.79 g/cc | ASTM D792 |
| Bulk Density | 0.961 g/cc | 0.0347 lb/in³ | |
| Water Absorption | 0.010 - 0.030 % @Time 86400 sec | 0.010 - 0.030 % @Time 24.0 hour | Immersion; ASTM D570 |
| Viscosity | 1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 1.50e+6 - 2.30e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt Viscosity; ASTM D3835 |
| Melt Flow | 6.0 - 25 g/10 min @Load 12.5 kg, Temperature 232 °C | 6.0 - 25 g/10 min @Load 27.6 lb, Temperature 450 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 - 80 | 75 - 80 | ASTM D2240 |
| Tensile Strength at Break | 34.0 - 55.0 MPa | 4930 - 7980 psi | ASTM D638 |
| Tensile Strength, Yield | 45.0 - 55.0 MPa | 6530 - 7980 psi | ASTM D638 |
| Elongation at Break | 50 - 200 % | 50 - 200 % | ASTM D638 |
| Elongation at Yield | 5.0 - 10 % | 5.0 - 10 % | ASTM D638 |
| Tensile Modulus | 1.379 - 2.31 GPa | 200.0 - 335 ksi | ASTM D638 |
| Flexural Strength | 58.0 - 76.0 MPa @Strain 5.00 % | 8410 - 11000 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 1.655 - 2.31 GPa | 240.0 - 335 ksi | ASTM D790 |
| Compressive Strength | 69.0 - 103 MPa | 10000 - 14900 psi | ASTM D695 |
| Izod Impact, Notched | 1.07 - 2.14 J/cm | 2.00 - 4.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.7 - 42.7 J/cm | 20.0 - 80.0 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.14 | 0.14 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.20 | 0.20 | vs. steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 9.0 | 5.0 - 9.0 | 1000 g pad; CS-17 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm @Temperature 20.0 °C | 2.00e+14 ohm-cm @Temperature 68.0 °F | 65% RH; ASTM D257 |
| Dielectric Constant | 4.5 @Frequency 1.00e+8 Hz | 4.5 @Frequency 1.00e+8 Hz | ASTM D150 |
| 9.5 @Frequency 100 Hz | 9.5 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 66.9 kV/mm | 1700 kV/in | ASTM D149 |
| Dissipation Factor | 0.010 - 0.21 @Frequency 100 Hz | 0.010 - 0.21 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 119 - 144 µm/m-°C | 66.0 - 80.0 µin/in-°F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.170 - 0.190 W/m-K | 1.18 - 1.32 BTU-in/hr-ft²-°F | ASTM D433 |
| Melting Point | 165 - 172 °C | 329 - 342 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 - 140 °C | 257 - 284 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 - 115 °C | 221 - 239 °F | ASTM D648 |
| Glass Transition Temp, Tg | -40.0 - -38.0 °C @Frequency 1.00 Hz | -40.0 - -36.4 °F @Frequency 1.00 Hz | DMA |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt loss / in air; TGA |
| 410 °C | 770 °F | 1% wt loss / in nitrogen; TGA | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 44 % | 44 % | ASTM D2868 |
| 60 % | 60 % | select grades; ASTM D2868 | |