- 密度 [g/cm3]: 1.76
- 弯曲模量 [MPa]: 0.425
- 脆化温度 [℃]: -37.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 | ||
| Water Absorption | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) | ||
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| 15 g/10 min @Load 5.00 kg, Temperature 230 °C | 15 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 475 % | 475 % | 50mm/min; ASTM D638 | ||
| Flexural Modulus | 0.425 GPa | 61.6 ksi | 2mm/min; ASTM D790 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | 10 mA, after 2 min; ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+14 ohm | >= 1.00e+14 ohm | < 1V after 2 min - 500 V; ASTM D257 | ||
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz | 7.0 @Frequency 1e+6 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 169 °C | 336 °F | ASTM D3418 | ||
| Brittleness Temperature | -37.0 °C | -34.6 °F | ASTM D746A | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | >= 100 % @Thickness 3.00 mm | >= 100 % @Thickness 0.118 in | limiting (sheet); ASTM D2863 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||