- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.79 g/cc | 1.79 g/cc | DIN 53 479 | ||
| Moisture Absorption at Equilibrium | <= 0.050 % | <= 0.050 % | Absorption of humidity in standard operating environment; DIN 53 715 | ||
| Water Absorption at Saturation | <= 0.050 % | <= 0.050 % | DIN 53 495 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 105 MPa @Time 30.0 sec | 15200 psi @Time 0.00833 hour | DIN 53 456 | ||
| Tensile Strength | 55.0 MPa | 7980 psi | DIN 53 455 | ||
| Elongation at Break | 20 - 400 % | 20 - 400 % | DIN 53 455 | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | DIN 53 457 | ||
| Flexural Modulus | 2.00 GPa | 290 ksi | from bending test; DIN 53 457 | ||
| Charpy Impact, Notched | NB | NB | DIN 53 453 | ||
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | Against steel, p=0.05 N/mm², v=0.6 m/s, hardened and ground | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.00e+14 ohm-cm | 4.00e+14 ohm-cm | DIN 53 482, VDE 0303, Part 3 | ||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | DIN 53 482 | ||
| Dielectric Constant | 8.0 @Frequency 1.00e+6 Hz | 8.0 @Frequency 1.00e+6 Hz | DIN 53 483, IEC-250 | ||
| Dielectric Strength | 17.0 - 150 kV/mm | 432 - 3810 kV/in | Breakdown; DIN 53 481, IEC-243, VDE 0303 Part 1 | ||
| Dielectric Loss Index | 0.060 @Frequency 1.00e+6 Hz | 0.060 @Frequency 1.00e+6 Hz | DIN 53 483, IEC-250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 130 µm/m-°C | 72.2 µin/in-°F | |||
| Specific Heat Capacity | 1.20 J/g-°C | 0.287 BTU/lb-°F | |||
| Thermal Conductivity | 0.110 W/m-K | 0.763 BTU-in/hr-ft²-°F | |||
| Melting Point | 178 °C | 352 °F | DIN 53 736 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | Short Periods | ||
| 150 °C | 302 °F | Continuous use | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO-R 75 Method B | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO-R 75 Method A | ||
| Glass Transition Temp, Tg | -18.0 °C | -0.400 °F | dynamic; DIN 53 736 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| Color | white | ||||
| Creep Resistance | Grade CTI 600 | DIN 53 480, IEC-112, VDE 0303 Part 1 | |||
| Resistance to hot water, suds | resistant | ||||