- 熔体流动速率 [g/10min]: 4.0
- 拉伸强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 | ||
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec | <= 0.040 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |||
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 70 - 75 @Thickness 2.00 mm, Time 1.00 sec | 70 - 75 @Thickness 0.0787 in, Time 0.000278 hour | ASTM D2240 | ||
| Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 2900 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 20.0 - 35.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C | 2900 - 5080 psi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Break | 200 - 600 % @Thickness 2.00 mm, Temperature 23.0 °C | 200 - 600 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Elongation at Yield | 10 - 12 % @Thickness 2.00 mm, Temperature 23.0 °C | 10 - 12 % @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 0.800 - 1.20 GPa @Thickness 2.00 mm, Temperature 23.0 °C | 116 - 174 ksi @Thickness 0.0787 in, Temperature 73.4 °F | Type IV, 1.0 mm/min; ASTM D638 | ||
| Impact | 150 - 200 @Thickness 4.00 mm | 150 - 200 @Thickness 0.157 in | J/m Charpy Notched Impact Strength; 2 m/s; ASTM D6110 | ||
| Coefficient of Friction, Dynamic | 0.15 - 0.35 | 0.15 - 0.35 | vs. Itself; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 | ||
| Taber Abrasion, mg/1000 Cycles | 5.0 - 15 @Load 1.00 kg | 5.0 - 15 @Load 2.20 lb | CS-10 Wheel; ASTM D4060 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 | ||
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 | ||
| Dielectric Constant | 7.0 - 10 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 7.0 - 10 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | ||
| Dielectric Strength | 0.787 - 0.984 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 20.0 - 25.0 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | ASTM D149 | ||
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.20 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| Heat of Fusion | 30.0 - 40.0 J/g | 12.9 - 17.2 BTU/lb | Crystallization Heat; ASTM D3417 | ||
| 35.0 - 40.0 J/g | 15.1 - 17.2 BTU/lb | ASTM D3417 | |||
| CTE, linear, Parallel to Flow | 180 µm/m-°C @Temperature 0.000 - 40.0 °C | 100 µin/in-°F @Temperature 32.0 - 104 °F | ASTM D696 | ||
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C | 0.287 BTU/lb-°F @Temperature 73.4 °F | ASTM E968 | ||
| 1.60 J/g-°C @Temperature 100 °C | 0.382 BTU/lb-°F @Temperature 212 °F | ASTM E968 | |||
| Thermal Conductivity | 0.190 W/m-K @Temperature 23.0 °C | 1.32 BTU-in/hr-ft²-°F @Temperature 73.4 °F | ASTM C177 | ||
| Melting Point | 158 - 162 °C | 316 - 324 °F | ASTM D3418 | ||
| Crystallization Temperature | 115 - 130 °C | 239 - 266 °F | Peak, DSC; ASTM D3418 | ||
| Vicat Softening Point | 90.0 - 105 °C | 194 - 221 °F | Rate A (50°C/h), Loading 2 (50 N); ASTM D1525 | ||
| Glass Transition Temp, Tg | -35.0 °C | -31.0 °F | ASTM D4065 | ||
| Flammability, UL94 | V-0 @Thickness 0.100 mm | V-0 @Thickness 0.00394 in | UL 94 | ||
| Oxygen Index | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | ASTM D2863 | ||
| Descriptive Properties | |||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| Features | Copolymer | ||||
| Good Flexibility | |||||
| Medium Viscosity | |||||
| Generic | PVDF | ||||
| Processing Method | Extrusion | ||||