Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer

Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer 物性表: Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer物性表及特性介绍,Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer注塑参数详情,如需Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 3.5
  • 密度 [g/cm3]: 1.78
  • 缺口冲击强度: 0.65
  • 拉伸强度 [MPa]: 53.0
  • 断裂伸长率 [%]: 77.0
  • 弯曲强度 [MPa]: 35.0
  • 弯曲模量 [MPa]: 2.10
  • 热变形温度 [℃]: 147.0
 
Physical PropertiesMetricEnglishComments
Density 1.78 g/cc0.0643 lb/in³ISO 1183
Water Absorption <= 0.040 %<= 0.040 %ISO 62 (method 1)
Linear Mold Shrinkage 0.020 - 0.030 cm/cm0.020 - 0.030 in/in
Melt Flow  3.5 g/10 min
@Load 2.16 kg,
Temperature 230 °C
3.5 g/10 min
@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
 10 g/10 min
@Load 5.00 kg,
Temperature 230 °C
10 g/10 min
@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 78
@Thickness 2.00 mm
78
@Thickness 0.0787 in
ASTM D2240
Tensile Strength, Ultimate 35.0 - 50.0 MPa5080 - 7250 psi50 mm/min; ASTM D638
Tensile Strength, Yield 53.0 - 57.0 MPa7690 - 8270 psi50 mm/min; ASTM D638
Elongation at Break 20 - 50 %20 - 50 %50 mm/min; ASTM D638
Elongation at Yield 5.0 - 10 %5.0 - 10 %50 mm/min; ASTM D638
Modulus of Elasticity 2.50 GPa363 ksi1 mm/min; ASTM D638
Flexural Yield Strength 77.0 MPa11200 psi2 mm/min; ASTM D790
Flexural Modulus 2.10 GPa305 ksi2 mm/min; ASTM D790
Izod Impact, Notched 0.650 J/cm
@Thickness 4.00 mm,
Temperature 23.0 °C
1.22 ft-lb/in
@Thickness 0.157 in,
Temperature 73.4 °F
Notched V 10 mm; ASTM D256
Coefficient of Friction 0.20 - 0.300.20 - 0.30ASTM D1894
Coefficient of Friction, Static 0.20 - 0.400.20 - 0.40ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0 - 105.0 - 10CS10 / 1 kg
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity >= 1.00e+14 ohm-cm>= 1.00e+14 ohm-cmIntensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483
Surface Resistance >= 1.00e+14 ohm>= 1.00e+14 ohmVoltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483
 
Thermal PropertiesMetricEnglishComments
Heat of Fusion 58.0 J/g25.0 BTU/lbCrystallization Heat
 67.0 J/g28.8 BTU/lb80°C to end of melting
CTE, linear 120 - 140 µm/m-°C
@Temperature 20.0 °C
66.7 - 77.8 µin/in-°F
@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.20 J/g-°C0.287 BTU/lb-°F
 1.60 J/g-°C
@Temperature 100 °C
0.382 BTU/lb-°F
@Temperature 212 °F
Thermal Conductivity 0.200 W/m-K1.39 BTU-in/hr-ft²-°FASTM C177
Melting Point 174 °C345 °FCrystallinity by DSC; ASTM D 3418
Crystallization Temperature 140 °C284 °F
Maximum Service Temperature, Air 375 - 400 °C707 - 752 °FThermal Stability via TGA : beginning - and at 1% weight loss in air
Deflection Temperature at 0.46 MPa (66 psi) 147 °C
@Thickness 4.00 mm
297 °F
@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 113 °C
@Thickness 4.00 mm
235 °F
@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Vicat Softening Point 171 °C
@Load 1.00 kg,
Thickness 4.00 mm
340 °F
@Load 2.20 lb,
Thickness 0.157 in
ISO 306
Brittleness Temperature 0.000 - 10.0 °C32.0 - 50.0 °FASTM D746A
Glass Transition Temp, Tg -30.0 °C-22.0 °FDMTA
Oxygen Index 44 %
@Thickness 3.00 mm
44 %
@Thickness 0.118 in
sheet; ASTM D2863

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-43512.html

免责声明: 本文 Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4