- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.83
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 56.0
- 断裂伸长率 [%]: 89.0
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 4.50
- 热变形温度 [℃]: 152.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.83 g/cc | 0.0661 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.070 % | <= 0.070 % | ISO 62 (method 1) |
| Linear Mold Shrinkage | 0.010 - 0.030 cm/cm | 0.010 - 0.030 in/in | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 6.0 g/10 min @Load 5.00 kg, Temperature 230 °C | 6.0 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 82 @Thickness 2.00 mm | 82 @Thickness 0.0787 in | ASTM D2240 |
| Tensile Strength, Ultimate | 40.0 - 60.0 MPa | 5800 - 8700 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 56.0 - 60.0 MPa | 8120 - 8700 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 20 - 30 % | 20 - 30 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 3.0 - 5.0 % | 3.0 - 5.0 % | 50 mm/min; ASTM D638 |
| Modulus of Elasticity | 4.20 GPa | 609 ksi | 1 mm/min; ASTM D638 |
| Flexural Yield Strength | 89.0 MPa | 12900 psi | 2 mm/min; ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 2 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm @Thickness 4.00 mm, Temperature 23.0 °C | 1.12 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F | Notched V 10 mm; ASTM D256 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 | 5.0 - 10 | CS10 / 1 kg |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | Intensity = 10 mA after 2 min @ 23°C; ASTM D 257; DIN 53483 |
| Surface Resistance | <= 1000 ohm | <= 1000 ohm | Voltage < 1 V after 2 min - 500 V; ASTM D 257/DIN 53483 |
| Thermal Properties | Metric | English | Comments |
| Heat of Fusion | 59.0 J/g | 25.4 BTU/lb | Crystallization Heat |
| 67.0 J/g | 28.8 BTU/lb | 80°C to end of melting | |
| CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C | 66.7 - 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 174 °C | 345 °F | Crystallinity by DSC; ASTM D 3418 |
| Crystallization Temperature | 140 °C | 284 °F | |
| Maximum Service Temperature, Air | 300 - 350 °C | 572 - 662 °F | Thermal Stability via TGA : beginning - and at 1% weight loss in air |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 4.00 mm | 306 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C @Thickness 4.00 mm | 313 °F @Thickness 0.157 in | after annealing 150°C 16 hr; ASTM D648 |
| Vicat Softening Point | 168 °C @Load 1.00 kg, Thickness 4.00 mm | 334 °F @Load 2.20 lb, Thickness 0.157 in | ISO 306 |
| Brittleness Temperature | >= 0.000 °C | >= 32.0 °F | ASTM D746A |