- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.01
- 弯曲模量 [MPa]: 1.79
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 52.1 MPa | 7550 psi | ASTM D882 |
| Elongation at Break | 160 % | 160 % | ASTM D882 |
| Tensile Modulus | 1.72 GPa | 250 ksi | ASTM D882 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Tear Strength | 284 kN/m | 1620 pli | ASTM D1004 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 8.15 - 10.46 @Frequency 1000 Hz | 8.15 - 10.46 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 76.0 kV/mm @Thickness 0.0762 mm | 1930 kV/in @Thickness 0.00300 in | ASTM D149 |
| Dissipation Factor | 0.0050 - 0.019 @Frequency 1000 Hz | 0.0050 - 0.019 @Frequency 1000 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 170 °C | 329 - 338 °F | DSC |
| Maximum Service Temperature, Air | 129 °C | 265 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | VTM-0 |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.42 | 1.42 | |