- 密度 [g/cm3]: 1.76
- 吸水率 [%]: 0.02
- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 96.5
- 断裂伸长率 [%]: 131
- 弯曲模量 [MPa]: 6.03
- 硬度: 104.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec | 0.020 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm | 0.0090 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Yield | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 6.03 GPa | 875 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm | 2.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |