- 密度 [g/cm3]: 1.78
- 吸水率 [%]: 0.03
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 48.3
- 断裂伸长率 [%]: 55.2
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 48.3 MPa | 7000 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Tensile Modulus | 1.72 GPa | 250 ksi | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 8.5 @Frequency 1000 Hz | 8.5 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 10.2 kV/mm | 260 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 117 µm/m-°C @Temperature 20.0 °C | 65.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 168 °C | 335 °F | ASTM D4591 |
| Maximum Service Temperature, Air | 138 °C | 280 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |