Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride

Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride 物性表: Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride物性表及特性介绍,Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride注塑参数详情,如需Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 8.0
  • 密度 [g/cm3]: 1.77
  • 吸水率 [%]: 0.02
  • 缺口冲击强度: 0.8
  • 拉伸强度 [MPa]: 34.0
  • 断裂伸长率 [%]: 55.0
  • 弯曲强度 [MPa]: 35.0
  • 弯曲模量 [MPa]: 1.73
  • 脆化温度 [℃]: -30.0
 
Physical PropertiesMetricEnglishComments
Density 1.77 - 1.79 g/cc0.0639 - 0.0647 lb/in³ASTM D792
Water Absorption 0.020 %0.020 %ASTM D570
Linear Mold Shrinkage 0.025 - 0.030 cm/cm0.025 - 0.030 in/in
Melt Flow 8.0 - 10 g/10 min
@Load 3.80 kg
8.0 - 10 g/10 min
@Load 8.38 lb
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 76 - 8076 - 80ASTM D2240
Tensile Strength, Ultimate 35.0 - 45.0 MPa5080 - 6530 psiASTM D638
Tensile Strength, Yield 34.0 - 48.0 MPa4930 - 6960 psiASTM D638
Elongation at Break 50 - 250 %50 - 250 %ASTM D638
Elongation at Yield 10 %10 %ASTM D638
Tensile Modulus 1.70 - 3.10 GPa247 - 450 ksiASTM D638
Flexural Yield Strength 55.0 - 76.0 MPa7980 - 11000 psiASTM D790
Flexural Modulus 1.73 - 2.41 GPa251 - 350 ksiASTM D790
Izod Impact, Notched 0.800 - 1.30 J/cm1.50 - 2.44 ft-lb/in
Izod Impact, Unnotched >= 15.0 J/cm>= 28.1 ft-lb/inLow Temp; ASTM D256
Coefficient of Friction, Dynamic 0.12 - 0.150.12 - 0.15ASTM D1894
Coefficient of Friction, Static 0.10 - 0.150.10 - 0.15ASTM D1894
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.25e+15 ohm-cm1.25e+15 ohm-cmASTM D257
Dielectric Constant  5.6
@Frequency 1e+6 Hz
5.6
@Frequency 1e+6 Hz
ASTM D150
 6.9
@Frequency 60 Hz
6.9
@Frequency 60 Hz
ASTM D150
Dielectric Strength 13.0 kV/mm
@Thickness 3.20 mm
330 kV/in
@Thickness 0.126 in
Short-Time 500 V/sec
Dissipation Factor  0.035
@Frequency 60 Hz
0.035
@Frequency 60 Hz
ASTM D150
 0.158
@Frequency 1e+6 Hz
0.158
@Frequency 1e+6 Hz
ASTM D150
Arc Resistance >= 50 sec>= 50 secASTM D495
 
Thermal PropertiesMetricEnglishComments
CTE, linear 100 - 120 µm/m-°C
@Temperature 20.0 °C
55.6 - 66.7 µin/in-°F
@Temperature 68.0 °F
ASTM D696
Specific Heat Capacity 1.50 J/g-°C0.359 BTU/lb-°FDSC
Thermal Conductivity 0.190 - 0.220 W/m-K1.32 - 1.53 BTU-in/hr-ft²-°FASTM C177
Melting Point 165 - 168 °C329 - 334 °FASTM D3418
Maximum Service Temperature, Air 150 °C302 °FNo oxidative or thermal degradation after 5 years at 150°C (300°F)
Deflection Temperature at 1.8 MPa (264 psi) 105 - 115 °C221 - 239 °FTMA
Brittleness Temperature <= -30.0 °C<= -22.0 °FASTM D2236
Flammability, UL94 V-0V-0
Oxygen Index 44 %44 %ASTM D2863
 
Optical PropertiesMetricEnglishComments
Refractive Index 1.421.42
 
Processing PropertiesMetricEnglishComments
Processing Temperature 215 - 232 °C419 - 450 °FPreheat

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-43531.html

免责声明: 本文 Solvay Specialty Polymers Hylar® MP10 PVDF Polyvinylidene Fluoride 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4