- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.02
- 缺口冲击强度: 0.854
- 拉伸强度 [MPa]: 93.1
- 断裂伸长率 [%]: 117
- 弯曲模量 [MPa]: 8.55
- 硬度: 106.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec | 0.020 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm | 0.0050 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 93.1 MPa | 13500 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm | 1.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 335 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |