- 缺口冲击强度: 0.587
- 拉伸强度 [MPa]: 77.9
- 弯曲模量 [MPa]: 11.8
- 热变形温度 [℃]: 166.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | Method A; ASTM D792 | ||
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm | 0.010 - 0.013 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 77.9 MPa | 11300 psi | ASTM D638 | ||
| Tensile Strength, Yield | 77.9 MPa | 11300 psi | ASTM D638 | ||
| Elongation at Break | 0.80 % | 0.80 % | ASTM D638 | ||
| Elongation at Yield | 0.80 % | 0.80 % | ASTM D638 | ||
| Tensile Modulus | 14.3 GPa | 2070 ksi | ASTM D638 | ||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 | ||
| Flexural Modulus | 11.8 GPa | 1710 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.587 J/cm @Thickness 3.18 mm | 1.10 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Unnotched | 2.03 J/cm @Thickness 3.18 mm | 3.80 ft-lb/in @Thickness 0.125 in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 14.6 kJ/m² | 6.95 ft-lb/in² | ISO 180 | ||
| Falling Dart Impact | 11.4 J | 8.41 ft-lb | ASTM D3763 | ||
| Impact Test | 3.01 J | 2.22 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C @Temperature 20.0 °C | 17.2 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 | ||
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 20.0 °C | 47.2 µin/in-°F @Temperature 68.0 °F | TMA; ASTM E831 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 331 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 - 232 °C | 424 - 450 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |||
| Descriptive Properties | |||||
| Color | Black | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.