- 密度 [g/cm3]: 0.85
- 弯曲强度 [MPa]: 18.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.850 - 2.28 g/cc | 0.0307 - 0.0824 lb/in³ | Average value: 1.95 g/cc Grade Count:16 |
| Solids Content | 58.0 - 60.0 % | 58.0 - 60.0 % | Average value: 59.3 % Grade Count:4 |
| Apparent Bulk Density | 0.300 - 0.350 g/cc | 0.0108 - 0.0126 lb/in³ | Average value: 0.322 g/cc Grade Count:4 |
| Particle Size | 0.100 - 675 µm | 0.100 - 675 µm | Average value: 232 µm Grade Count:35 |
| pH | 9.00 - 9.50 | 9.00 - 9.50 | Average value: 9.13 Grade Count:4 |
| Specific Surface Area | 2.50 - 20.0 m²/g | 2.50 - 20.0 m²/g | Average value: 7.01 m²/g Grade Count:9 |
| Viscosity | 22.0 - 47.0 cP | 22.0 - 47.0 cP | Average value: 31.3 cP Grade Count:3 |
| Linear Mold Shrinkage | 0.0260 - 0.0470 cm/cm | 0.0260 - 0.0470 in/in | Average value: 0.0357 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 18.6 - 42.0 MPa | 2700 - 6090 psi | Average value: 28.9 MPa Grade Count:22 |
| Elongation at Break | 250 - 500 % | 250 - 500 % | Average value: 326 % Grade Count:22 |
| Coefficient of Friction | 0.100 | 0.100 | Average value: 0.100 Grade Count:5 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 2.10 - 100 kV/mm | 53.3 - 2540 kV/in | Average value: 34.5 kV/mm Grade Count:8 |
| Dissipation Factor | 0.000300 | 0.000300 | Average value: 0.000300 Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 320 - 334 °C | 608 - 633 °F | Average value: 327 °C Grade Count:17 |
| Crystallization Temperature | 310 - 318 °C | 590 - 604 °F | Average value: 314 °C Grade Count:5 |
| Processing Properties | Metric | English | Comments |
| Moisture Content | 0.0400 % | 0.0400 % | Average value: 0.0400 % Grade Count:9 |
| Injection Pressure | 16.0 - 30.0 MPa | 2320 - 4350 psi | Average value: 23.0 MPa Grade Count:6 |