- 缺口冲击强度: 1.52
- 拉伸强度 [MPa]: 24.5
- 脆化温度 [℃]: -200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.13 - 2.23 g/cc | 2.13 - 2.23 g/cc | ASTM D1457-18; ISO.1183 DN.53479 | ||
| Deformation | 9.5 - 11 % | 9.5 - 11 % | 230°C, 1 day, 140 kg/cm^2; ASTM D621 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 53 - 57 | 53 - 57 | ASTM D2240; DIN.53505 | ||
| Ball Indentation Hardness | 30.0 MPa | 4350 psi | ISO.2039-2 | ||
| Tensile Strength, Yield | 24.5 - 29.4 MPa | 3560 - 4270 psi | ASTM D1708 | ||
| 25.0 - 30.0 MPa | 3630 - 4350 psi | ISO.527 DN.53455 | |||
| Elongation at Break | 250 - 300 % | 250 - 300 % | ASTM D1708 | ||
| Elongation at Yield | 25 % | 25 % | ISO.527 DN.53455 | ||
| Izod Impact, Notched | 1.52 J/cm | 2.85 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO.167 DN.53482 | ||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | ISO.167 DN.53482 | ||
| Dielectric Strength | 50.0 - 80.0 kV/mm | 1270 - 2030 kV/in | ASTM D149; ISO.243 DN.53481 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 - 140 µm/m-°C @Temperature 20.0 °C | 66.7 - 77.8 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Thermal Conductivity | 0.4068 W/m-K | 2.818 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Melting Point | 325 - 330 °C | 617 - 626 °F | ISO.3146 | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | ISO.75 DN.53461 | ||
| Minimum Service Temperature, Air | -250 °C | -418 °F | |||
| Brittleness Temperature | -200 °C | -328 °F | |||
| Descriptive Properties | |||||
| Corrosion | 20 - 25 cc-dak/kg-ms | 25 - 1000°C | |||
| Kinding Temperature | 530 | °C, ASTM D1929 | |||