- 密度 [g/cm3]: 3.9
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 3.90 g/cc | 0.141 lb/in³ | ASTM 1457-62 T |
Deformation | 5.0 % | 5.0 % | 14 MPa, 100 h, 23°C; ASTM D621-59 |
Mechanical Properties | Metric | English | Comments |
Ball Indentation Hardness | 40.0 MPa | 5800 psi | ASTM 1457-62 T |
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM 1457-62 T |
Elongation at Break | >= 100 % | >= 100 % | ASTM 1457-62 T |
Coefficient of Friction, Dynamic | 0.16 - 0.19 | 0.16 - 0.19 | v = 1 m/s |
0.18 - 0.20 | 0.18 - 0.20 | v = 1.9 m/s | |
Abrasion | 0.20 | 0.20 | mm of depth after 200 hrs load duration; Partner Material ST 50 |
Electrical Properties | Metric | English | Comments |
Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | DIN 53482 |
Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | DIN 53482 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 70.0 µm/m-°C @Temperature 100 °C | 38.9 µin/in-°F @Temperature 212 °F | DIN 52328 |
Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | DIN 52612 |