- 密度 [g/cm3]: 3.9
- 缺口冲击强度: 1.4
- 拉伸强度 [MPa]: 15.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.90 g/cc | 0.141 lb/in³ | ISO 1183 |
| Filler Content | 60 % | 60 % | Bronze Filler |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ISO 868 |
| Ball Indentation Hardness | 52.0 MPa | 7540 psi | ISO 2039-1 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ISO 527 |
| Elongation at Break | 220 % | 220 % | ISO 527 |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 360 °C | 680 °F | Molding |
| Back Pressure | 60.0 - 80.0 MPa | 8700 - 11600 psi | Molding Pressure |