- 密度 [g/cm3]: 2.15
- 缺口冲击强度: 1.4
- 拉伸强度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in³ | |
| Density | 2.15 g/cc | 0.0777 lb/in³ | ISO 1183 |
| Particle Size | 800 µm | 800 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Ball Indentation Hardness | 34.0 MPa | 4930 psi | ISO 2039-1 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 250 % | 250 % | ISO 527 |
| Izod Impact, Notched | 1.40 J/cm | 2.62 ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.10e+18 ohm-cm | 1.10e+18 ohm-cm | IEC 60093 |
| Surface Resistance | 4.50e+17 ohm | 4.50e+17 ohm | IEC 60093 |
| Dielectric Constant | 2.1 | 2.1 | IEC 60250 |
| Dielectric Strength | 72.0 kV/mm | 1830 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00010 | 0.00010 | IEC 60250 |
| Arc Resistance | 420 sec | 420 sec | IEC 61621 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 125 µm/m-°C @Temperature 20.0 °C | 69.4 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Specific Heat Capacity | 1.00 J/g-°C | 0.239 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 35.0 - 40.0 MPa | 5080 - 5800 psi | Molding Pressure |