- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.49
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 28.0
- 断裂伸长率 [%]: 7.00
- 弯曲强度 [MPa]: 38.6
- 弯曲模量 [MPa]: 0.230
- 硬度: 110.0
- 热变形温度 [℃]: 53.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.19 g/cc | 0.0371 - 0.0430 lb/in³ | Average value: 1.13 g/cc Grade Count:64 |
| Water Absorption | 0.490 - 10.5 % | 0.490 - 10.5 % | Average value: 3.91 % Grade Count:47 |
| Moisture Absorption at Equilibrium | 0.250 - 5.00 % | 0.250 - 5.00 % | Average value: 2.91 % Grade Count:32 |
| Water Absorption at Saturation | 4.50 - 9.00 % | 4.50 - 9.00 % | Average value: 8.28 % Grade Count:19 |
| Oxygen Transmission Rate | 21.0 - 198 cc/m²/day | 1.35 - 12.8 cc/100 in²/day | Average value: 51.2 cc/m²/day Grade Count:13 |
| Nitrogen Transmission | 7.80 cc-mm/m²-24hr-atm | 19.8 cc-mil/100 in²-24hr-atm | Average value: 7.80 cc-mm/m²-24hr-atm Grade Count:10 |
| Carbon Dioxide Transmission | 113 cc-mm/m²-24hr-atm | 287 cc-mil/100 in²-24hr-atm | Average value: 113 cc-mm/m²-24hr-atm Grade Count:10 |
| Viscosity | 3.30 - 4.50 cP | 3.30 - 4.50 cP | Average value: 3.86 cP Grade Count:11 |
| Viscosity Measurement | 0.750 - 260 | 0.750 - 260 | Average value: 79.7 Grade Count:25 |
| Viscosity Test | 150 - 250 cm³/g | 150 - 250 cm³/g | Average value: 203 cm³/g Grade Count:9 |
| Maximum Moisture Content | 0.00100 - 0.0800 | 0.00100 - 0.0800 | Average value: 0.0668 Grade Count:12 |
| Linear Mold Shrinkage | 0.00300 - 0.0230 cm/cm | 0.00300 - 0.0230 in/in | Average value: 0.0117 cm/cm Grade Count:28 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0130 cm/cm | 0.00200 - 0.0130 in/in | Average value: 0.00778 cm/cm Grade Count:6 |
| Melt Flow | 1.20 - 162 g/10 min | 1.20 - 162 g/10 min | Average value: 46.6 g/10 min Grade Count:15 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 - 119 | 110 - 119 | Average value: 116 Grade Count:11 |
| Ball Indentation Hardness | 90.0 - 170 MPa | 13100 - 24700 psi | Average value: 121 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 38.6 - 93.1 MPa | 5600 - 13500 psi | Average value: 68.3 MPa Grade Count:16 |
| Tensile Strength, Yield | 28.0 - 90.0 MPa | 4060 - 13100 psi | Average value: 64.5 MPa Grade Count:29 |
| Film Elongation at Break, MD | 510 - 540 % | 510 - 540 % | Average value: 533 % Grade Count:4 |
| Film Elongation at Break, TD | 550 - 560 % | 550 - 560 % | Average value: 555 % Grade Count:4 |
| Elongation at Break | 5.00 - 450 % | 5.00 - 450 % | Average value: 108 % Grade Count:27 |
| Elongation at Yield | 3.70 - 150 % | 3.70 - 150 % | Average value: 31.5 % Grade Count:19 |
| Modulus of Elasticity | 0.210 - 3.77 GPa | 30.5 - 547 ksi | Average value: 2.34 GPa Grade Count:27 |
| Flexural Yield Strength | 7.00 - 140 MPa | 1020 - 20300 psi | Average value: 76.3 MPa Grade Count:29 |
| 30.0 - 30.0 MPa @Temperature 90.0 - 90.0 °C | 4350 - 4350 psi @Temperature 194 - 194 °F | Average value: 30.0 MPa Grade Count:1 | |
| Flexural Modulus | 0.230 - 3.50 GPa | 33.4 - 508 ksi | Average value: 2.18 GPa Grade Count:32 |
| 0.850 - 0.850 GPa @Temperature 90.0 - 90.0 °C | 123 - 123 ksi @Temperature 194 - 194 °F | Average value: 0.850 GPa Grade Count:1 | |
| Secant Modulus, MD | 0.190 - 0.210 GPa | 27.6 - 30.5 ksi | Average value: 0.200 GPa Grade Count:4 |
| Secant Modulus, TD | 0.200 - 0.230 GPa | 29.0 - 33.4 ksi | Average value: 0.208 GPa Grade Count:4 |
| Izod Impact, Notched | 0.400 - 7.47 J/cm | 0.749 - 14.0 ft-lb/in | Average value: 2.31 J/cm Grade Count:16 |
| 1.0678 - 2.1356 J/cm @Temperature -40.0 - -20.0 °C | 2.0004 - 4.0009 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 1.51 J/cm Grade Count:2 | |
| 1.0678 - 2.1356 J/cm @Thickness 3.17 - 3.17 mm | 2.0004 - 4.0009 ft-lb/in @Thickness 0.125 - 0.125 in | Average value: 1.51 J/cm Grade Count:2 | |
| Izod Impact, Notched (ISO) | 3.00 - 90.0 kJ/m² | 1.43 - 42.8 ft-lb/in² | Average value: 16.4 kJ/m² Grade Count:8 |
| 2.50 - 85.0 kJ/m² @Temperature -30.0 - -30.0 °C | 1.19 - 40.4 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 30.3 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 4.50 J/cm² - NB | 21.4 ft-lb/in² - NB | Average value: 8.15 J/cm² Grade Count:19 |
| 3.60 J/cm² - NB @Temperature -40.0 - -20.0 °C | 17.1 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 5.80 J/cm² Grade Count:7 | |
| Charpy Impact, Notched | 0.300 J/cm² - NB | 1.43 ft-lb/in² - NB | Average value: 1.20 J/cm² Grade Count:17 |
| 0.300 J/cm² - NB @Temperature -40.0 - -20.0 °C | 1.43 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 2.08 J/cm² Grade Count:7 | |
| Coefficient of Friction | 0.210 - 0.510 | 0.210 - 0.510 | Average value: 0.357 Grade Count:6 |
| Coefficient of Friction, Static | 0.280 - 0.940 | 0.280 - 0.940 | Average value: 0.507 Grade Count:4 |
| Film Tensile Strength at Break, MD | 40.0 - 42.0 MPa | 5800 - 6090 psi | Average value: 41.0 MPa Grade Count:4 |
| Film Tensile Strength at Break, TD | 39.0 - 43.0 MPa | 5660 - 6240 psi | Average value: 40.5 MPa Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+15 ohm-cm | 1.00e+9 - 1.00e+15 ohm-cm | Average value: 5.90e+14 ohm-cm Grade Count:23 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 2.84e+14 ohm Grade Count:10 |
| Dielectric Constant | 3.60 - 8.00 | 3.60 - 8.00 | Average value: 4.47 Grade Count:8 |
| Dielectric Strength | 17.3 - 120 kV/mm | 440 - 3050 kV/in | Average value: 26.9 kV/mm Grade Count:17 |
| Dissipation Factor | 0.0200 - 0.300 | 0.0200 - 0.300 | Average value: 0.0580 Grade Count:9 |
| Comparative Tracking Index | 500 - 600 V | 500 - 600 V | Average value: 592 V Grade Count:16 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.800 - 200 µm/m-°C | 0.444 - 111 µin/in-°F | Average value: 83.6 µm/m-°C Grade Count:18 |
| CTE, linear, Transverse to Flow | 0.800 - 200 µm/m-°C | 0.444 - 111 µin/in-°F | Average value: 97.0 µm/m-°C Grade Count:3 |
| Thermal Conductivity | 0.260 - 0.330 W/m-K | 1.80 - 2.29 BTU-in/hr-ft²-°F | Average value: 0.295 W/m-K Grade Count:4 |
| Melting Point | 185 - 262 °C | 365 - 504 °F | Average value: 211 °C Grade Count:52 |
| Maximum Service Temperature, Air | 80.0 - 200 °C | 176 - 392 °F | Average value: 127 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 53.0 - 220 °C | 127 - 428 °F | Average value: 167 °C Grade Count:21 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 210 °C | 104 - 410 °F | Average value: 71.5 °C Grade Count:31 |
| Vicat Softening Point | 68.0 - 245 °C | 154 - 473 °F | Average value: 197 °C Grade Count:8 |
| Decomposition Temperature | 300 °C | 572 °F | Average value: 300 °C Grade Count:10 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:20 |
| Oxygen Index | 27.0 - 37.0 % | 27.0 - 37.0 % | Average value: 30.7 % Grade Count:3 |
| Glow Wire Test | 750 - 960 °C | 1380 - 1760 °F | Average value: 908 °C Grade Count:3 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.50 - 12.4 % | 9.50 - 12.4 % | Average value: 11.0 % Grade Count:4 |
| Gloss | 101 - 124 % | 101 - 124 % | Average value: 114 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 30.0 - 250 °C | 86.0 - 482 °F | Average value: 221 °C Grade Count:8 |
| Adapter Temperature | 243 - 250 °C | 469 - 482 °F | Average value: 247 °C Grade Count:10 |
| Die Temperature | 230 - 245 °C | 446 - 473 °F | Average value: 240 °C Grade Count:12 |
| Melt Temperature | 200 - 280 °C | 392 - 536 °F | Average value: 243 °C Grade Count:23 |
| Mold Temperature | 20.0 - 90.0 °C | 68.0 - 194 °F | Average value: 61.8 °C Grade Count:8 |
| Drying Temperature | 60.0 - 85.0 °C | 140 - 185 °F | Average value: 73.5 °C Grade Count:7 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 5.60 hour Grade Count:5 |
| Moisture Content | 0.000 - 0.150 % | 0.000 - 0.150 % | Average value: 0.0832 % Grade Count:16 |