- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 1.3
- 弯曲模量 [MPa]: 2.40
- 热变形温度 [℃]: 160.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 6.0 % | 5.0 - 6.0 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.011 - 0.023 cm/cm | 0.011 - 0.023 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 120 MPa | 17400 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 35.0 MPa | 5080 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | DIN 53453 | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | DIN 53453 |
| 0.500 J/cm² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DIN 53453 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 500 V | 500 V | CTI 100; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |