Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer

Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer 物性表: Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer物性表及特性介绍,Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer注塑参数详情,如需Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.17
  • 吸水率 [%]: 1.5
  • 缺口冲击强度: 2.5
  • 拉伸强度 [MPa]: 80.0
  • 断裂伸长率 [%]: 110
  • 弯曲模量 [MPa]: 3.00
  • 热变形温度 [℃]: 207.0
 
Physical PropertiesMetricEnglishComments
Density 1.17 g/cc0.0423 lb/in³ASTM D792, ISO 1183
Water Absorption 1.5 %1.5 %23°C, 24h in H2O; sim. ISO 62
Water Absorption at Saturation 7.5 %7.5 %sim. ISO 62
Linear Mold Shrinkage, Flow 0.013 cm/cm0.013 in/inparallel; Euronil
Linear Mold Shrinkage, Transverse 0.013 cm/cm0.013 in/inEuronil
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 80.0 MPa11600 psiISO 527, ASTM D638
Elongation at Break 5.0 %5.0 %
Tensile Modulus 3.60 GPa522 ksiISO 527, ASTM D638
Flexural Yield Strength 110 MPa16000 psiISO 178, ASTM D790
 30.0 MPa
@Temperature 90.0 °C
4350 psi
@Temperature 194 °F
ISO 178, ASTM D790
Flexural Modulus 3.00 GPa435 ksiISO 178, ASTM D790
 0.850 GPa
@Temperature 90.0 °C
123 ksi
@Temperature 194 °F
ISO 178, ASTM D790
Izod Impact, Notched (ISO)  2.50 kJ/m²
@Temperature -30.0 °C
1.19 ft-lb/in²
@Temperature -22.0 °F
ISO 180/1A
 3.50 kJ/m²
@Temperature 23.0 °C
1.67 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 4.50 J/cm²21.4 ft-lb/in²ISO 179
 3.60 J/cm²
@Temperature -30.0 °C
17.1 ft-lb/in²
@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.450 J/cm²2.14 ft-lb/in²ISO 179
 0.350 J/cm²
@Temperature -30.0 °C
1.67 ft-lb/in²
@Temperature -22.0 °F
ISO 179
 
Electrical PropertiesMetricEnglishComments
Dielectric Strength 18.0 kV/mm
@Thickness 2.00 mm
457 kV/in
@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index  >= 600 V
@Thickness 3.20 mm
>= 600 V
@Thickness 0.126 in
Sol. B; IEC 112, UL 746A
 >= 600 V
@Thickness 3.20 mm
>= 600 V
@Thickness 0.126 in
Sol. A; IEC 112, UL 746A
 
Thermal PropertiesMetricEnglishComments
Maximum Service Temperature, Air 120 °C248 °F20,000 hr; IEC 216
Deflection Temperature at 0.46 MPa (66 psi) 207 °C405 °FISO 75, ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C176 °FISO 75, ASTM D648
Vicat Softening Point 220 °C428 °F49 N; ISO 306, ASTM D1525
 235 °C455 °F9.8 N; ISO 306, ASTM D1525
Flammability, UL94  V-0
@Thickness 0.800 mm
V-0
@Thickness 0.0315 in
 V-0
@Thickness 0.400 mm
V-0
@Thickness 0.0157 in
 V-0
@Thickness 1.60 mm
V-0
@Thickness 0.0630 in
 V-0
@Thickness 3.20 mm
V-0
@Thickness 0.126 in
Oxygen Index 28 %28 %ASTM D2863
Glow Wire Test  960 °C
@Thickness 0.800 mm
1760 °F
@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 694-2-12
 960 °C
@Thickness 3.20 mm
1760 °F
@Thickness 0.126 in
Glow Wire Flammability Index; IEC 694-2-12
 
Processing PropertiesMetricEnglishComments
Nozzle Temperature 270 - 280 °C518 - 536 °F
Zone 1 260 - 270 °C500 - 518 °Fhopper
Zone 2 260 - 275 °C500 - 527 °F
Zone 3 270 - 280 °C518 - 536 °F
Zone 4 270 - 280 °C518 - 536 °F
Melt Temperature 265 - 280 °C509 - 536 °FDo not melt above 280°C
Mold Temperature >= 80.0 °C>= 176 °F
Drying Temperature 80.0 - 85.0 °C176 - 185 °F
Dry Time 4 hour4 hour
Injection Pressure 70.0 - 100 MPa10200 - 14500 psi
 
Descriptive Properties
Clamping Forcein tons, 0.7 times the projected surface area in cm2
Flammability RatingSEFMVSS No. 302, 355x100x1 mm
Heat Resistance - Ball TestOKat 125°C, IEC 309
 OKat 165°C, IEC 309
Holding Pressure90 MPa
Needle TestOKIEC 695-2-2, 1 or 2 mm

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44387.html

免责声明: 本文 Nilit Nilamid A H2 FR HF2 Unfilled, Flame Retardant PA66/6 Co-Polymer 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4