- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 8.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO.1183 DIN.53479 |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 50% relative humidity |
| Water Absorption at Saturation | 8.4 % | 8.4 % | 23°C |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 88 | 88 | dry sample; ISO2039.2 |
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO2039.1 DIN.53456 |
| Tensile Strength at Break | 86.0 MPa | 12500 psi | ISO.527 DIN.53455 |
| Elongation at Break | 45 % | 45 % | ISO.527 DIN.53455 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ISO.527 DIN.53455 |
| Compressive Strength | 20.0 MPa | 2900 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
| Charpy Impact Unnotched | NB | NB | 7.5 J; ISO.R179 DIN.53453 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO179/3C DIN.53453 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | on dry ground steel; load =0.05MPa; speed =0.6 m/s |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ISO.93 DIN.53482 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | ISO.250 DIN.53483 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | ISO.243 DIN.53481 |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz | 0.060 @Frequency 1e+6 Hz | ISO.250 DIN.53483 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 47.2 µin/in-°F @Temperature 73.4 - 140 °F | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | DIN.52612 |
| Melting Point | 240 °C | 464 °F | |
| Maximum Service Temperature, Air | 92.0 °C | 198 °F | Maximum operating temperature continuously for 5000 hours based on a tensile stress of 50% at 23° C. |
| 160 °C | 320 °F | short period, no load | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | ISO.75 DIN.53461 |
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | impact conditions and heavy loads not considered |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| V-2 @Thickness 6.00 mm | V-2 @Thickness 0.236 in | ||
| Oxygen Index | 27 % | 27 % | ISO.4589 |