- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.43
- 拉伸强度 [MPa]: 60.0
- 断裂伸长率 [%]: 44.0
- 弯曲模量 [MPa]: 1.034
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 176 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO METHOD 527 |
| Elongation at Break | >= 300 % | >= 300 % | ISO METHOD 527 |
| Flexural Yield Strength | 44.0 MPa | 6380 psi | ISO METHOD 176 |
| Flexural Modulus | 1.034 GPa | 150.0 ksi | ISO METHOD 178 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ISO METHOD 180 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 198 °C | 388 °F | ISO METHOD 3146C |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 200 °C | 392 °F | |
| Middle Barrel Temperature | 230 °C | 446 °F | |
| Front Barrel Temperature | 250 °C | 482 °F | |
| Drying Temperature | 76.0 °C | 169 °F | |