- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 1.17
- 缺口冲击强度: 3.0
- 弯曲模量 [MPa]: 3.70
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.17 % @Temperature 23.0 °C, Time 86400 sec | 1.17 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 59.0 MPa | 8560 psi | ISO R 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO R 527 | ||
| Tensile Modulus | 4.30 GPa | 624 ksi | ISO R 527 | ||
| Flexural Strength | 100 MPa | 14500 psi | at break; ISO 178 | ||
| Flexural Modulus | 3.70 GPa | 537 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 243.5 °C | 470.3 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Descriptive Properties | |||||
| Compression Zone | 260-280°C | ||||
| Mixing Zone | 250-270°C | ||||