- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.6
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 3.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.6 % @Temperature 23.0 °C, Time 86400 sec | 1.6 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | Isotropy | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 type 1 A | ||
| Elongation at Break | 30 % | 30 % | ISO 527 Type 1A | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 type 1 A | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 | ||
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.030 | 0.030 | IEC 60250 | ||
| Comparative Tracking Index | 425 V | 425 V | Solution B; IEC 60112 | ||
| 525 V | 525 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| Oxygen Index | 23 % | 23 % | ISO 4589 | ||
| Glow Wire Test | 650 °C @Thickness 1.60 mm | 1200 °F @Thickness 0.0630 in | ISO 60695-2-12 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |||
| Front Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Melt Temperature | 242 °C | 468 °F | ISO 11357 | ||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 250-260°C | ||||