- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.3 % @Temperature 23.0 °C, Time 86400 sec | 1.3 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm | 0.016 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 Type 1A | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 type 1 A | ||
| Elongation at Break | 65 % | 65 % | ISO 527 Type 1A | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 | ||
| Flexural Modulus | 2.80 GPa | 406 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 3.4 | 3.4 | IEC 60250 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 85.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 185 °F | ISO 11359 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75/Af | ||
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | 1210 | ||
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | 1210 | |||
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | 1210 | |||
| Glow Wire Test | 700 °C @Thickness 0.800 mm | 1290 °F @Thickness 0.0315 in | ISO 60695-2-12 | ||
| 700 °C @Thickness 1.60 mm | 1290 °F @Thickness 0.0630 in | ISO 60695-2-12 | |||
| 750 °C @Thickness 3.20 mm | 1380 °F @Thickness 0.126 in | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |||
| Front Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 230-235°C | ||||