- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.1
- 缺口冲击强度: 0.65
- 拉伸强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 3.15
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183/A | ||
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec | 1.1 % @Temperature 73.4 °F, Time 24.0 hour | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 Type 1A | ||
| 80.0 MPa | 11600 psi | ASTM D638 | |||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ISO 527 type 1 A | ||
| 80.0 MPa | 11600 psi | ASTM D638 | |||
| Elongation at Break | 15 % | 15 % | ASTM D638 | ||
| 25 % | 25 % | ISO 527 Type 1A | |||
| Elongation at Yield | 3.5 % | 3.5 % | ISO 527 type 1 A | ||
| Tensile Modulus | 3.50 GPa | 508 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 | ||
| 200 MPa | 29000 psi | ISO 178 | |||
| Flexural Modulus | 3.15 GPa | 457 ksi | ISO 178 | ||
| 3.50 GPa | 508 ksi | ASTM D790 | |||
| Izod Impact, Notched | 0.650 J/cm | 1.22 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180/1eA | ||
| Charpy Impact Unnotched | 18.0 J/cm² | 85.7 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 | 3.5 | IEC 60250 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 | ||
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 | ||
| Comparative Tracking Index | 475 V | 475 V | Solution B; IEC 60112 | ||
| 600 V | 600 V | Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75/Af | ||
| Flammability, UL94 | V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | 1210 | ||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | 1210 | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | 1210 | |||
| V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | 1210 | |||
| Oxygen Index | 36 % | 36 % | ISO 4589 | ||
| Glow Wire Test | 700 °C @Thickness 0.800 mm | 1290 °F @Thickness 0.0315 in | ignition temperature; ISO 60695-2-13 | ||
| 700 °C @Thickness 1.60 mm | 1290 °F @Thickness 0.0630 in | ignition temperature; ISO 60695-2-13 | |||
| 700 °C @Thickness 3.20 mm | 1290 °F @Thickness 0.126 in | ignition temperature; ISO 60695-2-13 | |||
| 960 °C @Thickness 0.800 mm | 1760 °F @Thickness 0.0315 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 1.60 mm | 1760 °F @Thickness 0.0630 in | ISO 60695-2-12 | |||
| 960 °C @Thickness 3.20 mm | 1760 °F @Thickness 0.126 in | ISO 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 230 - 235 °C | 446 - 455 °F | |||
| Melt Temperature | 222 °C | 432 °F | ISO 11357 | ||
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 235-245°C | ||||
| Fire and smoke F index | I2/F3 | NF F 16 101 | |||
| Mixing Zone | 245-250°C | ||||