- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 1.2
- 缺口冲击强度: 1.3
- 断裂伸长率 [%]: 225
- 弯曲强度 [MPa]: 155.0
- 弯曲模量 [MPa]: 8.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | Approximate 24 hr. |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Flexural Yield Strength | 225 MPa | 32600 psi | ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.790 mm | HB @Thickness 0.0311 in | From Wellman QC Laboratory Testing; UL 94 |