- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.85
- 缺口冲击强度: 0.427
- 拉伸强度 [MPa]: 82.7
- 断裂伸长率 [%]: 110
- 弯曲强度 [MPa]: 103.0
- 弯曲模量 [MPa]: 2.96
- 硬度: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 - 1.87 g/cc | 0.0531 - 0.0676 lb/in³ | Average value: 1.69 g/cc Grade Count:18 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 25.0 % Grade Count:4 |
| Water Absorption | 0.850 - 2.00 % | 0.850 - 2.00 % | Average value: 1.14 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 1.10 - 2.10 % | 1.10 - 2.10 % | Average value: 1.40 % Grade Count:6 |
| Linear Mold Shrinkage | 0.00250 - 0.00800 cm/cm | 0.00250 - 0.00800 in/in | Average value: 0.00533 cm/cm Grade Count:9 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00400 - 0.0100 cm/cm | 0.00400 - 0.0100 in/in | Average value: 0.00625 cm/cm Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 - 120 | 100 - 120 | Average value: 113 Grade Count:6 |
| Tensile Strength, Ultimate | 103 - 200 MPa | 15000 - 29000 psi | Average value: 157 MPa Grade Count:13 |
| Tensile Strength, Yield | 82.7 - 131 MPa | 12000 - 19000 psi | Average value: 114 MPa Grade Count:5 |
| Elongation at Break | 1.00 - 5.50 % | 1.00 - 5.50 % | Average value: 2.75 % Grade Count:15 |
| Elongation at Yield | 3.00 - 3.80 % | 3.00 - 3.80 % | Average value: 3.53 % Grade Count:3 |
| Modulus of Elasticity | 5.86 - 18.0 GPa | 850 - 2610 ksi | Average value: 12.3 GPa Grade Count:13 |
| Flexural Yield Strength | 110 - 262 MPa | 16000 - 38000 psi | Average value: 190 MPa Grade Count:9 |
| Flexural Modulus | 2.96 - 13.4 GPa | 430 - 1950 ksi | Average value: 7.35 GPa Grade Count:9 |
| Izod Impact, Notched | 0.427 - 1.33 J/cm | 0.800 - 2.50 ft-lb/in | Average value: 0.848 J/cm Grade Count:9 |
| Izod Impact, Unnotched | 4.27 - 7.47 J/cm | 8.00 - 14.0 ft-lb/in | Average value: 5.87 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 2.50 - 7.50 J/cm² | 11.9 - 35.7 ft-lb/in² | Average value: 5.79 J/cm² Grade Count:7 |
| 5.00 - 5.00 J/cm² @Temperature -30.0 - -30.0 °C | 23.8 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.00 J/cm² Grade Count:4 | |
| Charpy Impact, Notched | 0.800 - 1.50 J/cm² | 3.81 - 7.14 ft-lb/in² | Average value: 1.19 J/cm² Grade Count:7 |
| 0.900 - 1.30 J/cm² @Temperature -30.0 - -30.0 °C | 4.28 - 6.19 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.13 J/cm² Grade Count:6 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+8 - 1.00e+15 ohm-cm | 1.00e+8 - 1.00e+15 ohm-cm | Average value: 1.13e+14 ohm-cm Grade Count:10 |
| Dielectric Strength | 20.0 - 30.0 kV/mm | 508 - 762 kV/in | Average value: 24.5 kV/mm Grade Count:10 |
| Comparative Tracking Index | 250 - 350 V | 250 - 350 V | Average value: 308 V Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 40.0 µm/m-°C | 11.1 - 22.2 µin/in-°F | Average value: 28.8 µm/m-°C Grade Count:10 |
| CTE, linear, Transverse to Flow | 60.0 - 80.0 µm/m-°C | 33.3 - 44.4 µin/in-°F | Average value: 76.7 µm/m-°C Grade Count:6 |
| Melting Point | 295 °C | 563 °F | Average value: 295 °C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 123 - 290 °C | 254 - 554 °F | Average value: 274 °C Grade Count:14 |
| UL RTI, Electrical | 130 - 140 °C | 266 - 284 °F | Average value: 138 °C Grade Count:6 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 293 - 321 °C | 560 - 610 °F | Average value: 307 °C Grade Count:4 |
| Mold Temperature | 79.4 - 149 °C | 175 - 300 °F | Average value: 114 °C Grade Count:4 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:4 |