- 密度 [g/cm3]: 1.87
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.87 g/cc | 0.0676 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 50% RH / 23°C; Similar to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 200 MPa | 29000 psi | ISO 527-1/-2 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1/-2 |
| Tensile Modulus | 18.0 GPa | 2610 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B |
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | |