- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 7.0
- 热变形温度 [℃]: 290.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | Humidity Absorption; Sim. to ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity Number | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 250 MPa | 36300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.7 % | 2.7 % | ISO 527-1/-2 | ||
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 8.00 J/cm² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.60 J/cm² @Temperature 23.0 °C | 7.61 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | IEC 60250 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00070 @Frequency 100 Hz | 0.00070 @Frequency 100 Hz | IEC 60250 | ||
| 0.0020 @Frequency 1e+6 Hz | 0.0020 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 | ||
| Vicat Softening Point | 290 °C | 554 °F | 50°C/h 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | Glass Transition Temperature (10°C/min); ISO 11357-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Oxygen Index | 22 % | 22 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Platable | Yes | ||||
| With Fillers | Yes | ||||