- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.7
- 缺口冲击强度: 0.25
- 拉伸强度 [MPa]: 30.0
- 断裂伸长率 [%]: 11.0
- 弯曲强度 [MPa]: 20.7
- 弯曲模量 [MPa]: 0.621
- 硬度: 78.0
- 热变形温度 [℃]: 60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 - 1.46 g/cc | 0.0368 - 0.0527 lb/in³ | Average value: 1.13 g/cc Grade Count:279 |
| Water Absorption | 0.700 - 9.00 % | 0.700 - 9.00 % | Average value: 4.55 % Grade Count:153 |
| Moisture Absorption at Equilibrium | 0.170 - 8.50 % | 0.170 - 8.50 % | Average value: 2.56 % Grade Count:111 |
| Water Absorption at Saturation | 6.50 - 9.00 % | 6.50 - 9.00 % | Average value: 8.20 % Grade Count:24 |
| Viscosity Measurement | 1.80 - 260 | 1.80 - 260 | Average value: 135 Grade Count:30 |
| Viscosity Test | 115 - 280 cm³/g | 115 - 280 cm³/g | Average value: 157 cm³/g Grade Count:14 |
| Linear Mold Shrinkage | 0.00100 - 0.0280 cm/cm | 0.00100 - 0.0280 in/in | Average value: 0.0139 cm/cm Grade Count:177 |
| Linear Mold Shrinkage, Transverse | 0.00122 - 0.0250 cm/cm | 0.00122 - 0.0250 in/in | Average value: 0.0141 cm/cm Grade Count:42 |
| Melt Flow | 2.00 - 148 g/10 min | 2.00 - 148 g/10 min | Average value: 46.1 g/10 min Grade Count:31 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 55.0 - 90.0 | 55.0 - 90.0 | Average value: 74.8 Grade Count:30 |
| Hardness, Rockwell R | 78.0 - 121 | 78.0 - 121 | Average value: 114 Grade Count:63 |
| Hardness, Shore D | 77.0 - 88.0 | 77.0 - 88.0 | Average value: 81.6 Grade Count:7 |
| Ball Indentation Hardness | 100 - 170 MPa | 14500 - 24700 psi | Average value: 141 MPa Grade Count:10 |
| Tensile Strength, Ultimate | 20.7 - 170 MPa | 3000 - 24700 psi | Average value: 73.6 MPa Grade Count:118 |
| 26.0 - 116 MPa @Temperature -40.0 - 120 °C | 3770 - 16800 psi @Temperature -40.0 - 248 °F | Average value: 55.6 MPa Grade Count:4 | |
| Tensile Strength, Yield | 30.0 - 98.0 MPa | 4350 - 14200 psi | Average value: 72.4 MPa Grade Count:174 |
| Elongation at Break | 2.00 - 1500 % | 2.00 - 1500 % | Average value: 62.0 % Grade Count:240 |
| Elongation at Yield | 3.40 - 100 % | 3.40 - 100 % | Average value: 16.6 % Grade Count:129 |
| Modulus of Elasticity | 0.700 - 9.55 GPa | 102 - 1390 ksi | Average value: 2.53 GPa Grade Count:157 |
| Flexural Yield Strength | 11.0 - 140 MPa | 1600 - 20300 psi | Average value: 94.6 MPa Grade Count:169 |
| 29.9922 - 140 MPa @Temperature -40.0 - 90.0 °C | 4350.01 - 20300 psi @Temperature -40.0 - 194 °F | Average value: 71.0 MPa Grade Count:4 | |
| Flexural Modulus | 0.621 - 8.55 GPa | 90.0 - 1240 ksi | Average value: 2.56 GPa Grade Count:211 |
| 0.350 - 4.30 GPa @Temperature -40.0 - 120 °C | 50.8 - 624 ksi @Temperature -40.0 - 248 °F | Average value: 1.39 GPa Grade Count:6 | |
| Compressive Yield Strength | 7.00 - 100 MPa | 1020 - 14500 psi | Average value: 46.3 MPa Grade Count:6 |
| Poissons Ratio | 0.380 - 0.450 | 0.380 - 0.450 | Average value: 0.410 Grade Count:5 |
| Shear Modulus | 1.06 - 1.21 GPa | 154 - 175 ksi | Average value: 1.10 GPa Grade Count:4 |
| Shear Strength | 50.0 - 65.0 MPa | 7250 - 9430 psi | Average value: 58.0 MPa Grade Count:3 |
| Izod Impact, Notched | 0.250 - 100 J/cm | 0.468 - 187 ft-lb/in | Average value: 1.10 J/cm Grade Count:120 |
| 0.250 - 2.40 J/cm @Temperature -40.0 - -20.0 °C | 0.468 - 4.50 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.708 J/cm Grade Count:7 | |
| 0.490332 - 0.490332 J/cm @Temperature 3.20 - 3.20 °C | 0.918594 - 0.918594 ft-lb/in @Temperature 37.8 - 37.8 °F | Average value: 0.708 J/cm Grade Count:1 | |
| 0.490332 - 0.490332 J/cm @Thickness 23.0 - 23.0 mm | 0.918594 - 0.918594 ft-lb/in @Thickness 0.906 - 0.906 in | Average value: 0.708 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 8.01 J/cm - NB | 15.0 ft-lb/in - NB | Average value: 10.9 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² - NB | 1.67 ft-lb/in² - NB | Average value: 14.0 kJ/m² Grade Count:83 |
| 3.50 - 50.0 kJ/m² @Temperature -40.0 - -30.0 °C | 1.67 - 23.8 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 13.9 kJ/m² Grade Count:21 | |
| Izod Impact, Unnotched (ISO) | 60.0 kJ/m² - NB | 28.6 ft-lb/in² - NB | Average value: 88.0 kJ/m² Grade Count:6 |
| NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:2 | |
| Charpy Impact Unnotched | 3.00 J/cm² - NB | 14.3 ft-lb/in² - NB | Average value: 11.0 J/cm² Grade Count:113 |
| 4.00 J/cm² - NB @Temperature -40.0 - -20.0 °C | 19.0 ft-lb/in² - NB @Temperature -40.0 - -4.00 °F | Average value: 11.4 J/cm² Grade Count:74 | |
| Charpy Impact, Notched | 0.100 - 1000 J/cm² | 0.476 - 4760 ft-lb/in² | Average value: 1.28 J/cm² Grade Count:121 |
| 0.100 - 3.10 J/cm² @Temperature -40.0 - -20.0 °C | 0.476 - 14.8 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 0.757 J/cm² Grade Count:75 | |
| Puncture Energy | 13.1 - 108 J | 9.66 - 79.7 ft-lb | Average value: 36.1 J Grade Count:6 |
| 5.10 - 60.0 J @Temperature -30.0 - -30.0 °C | 3.76 - 44.3 ft-lb @Temperature -22.0 - -22.0 °F | Average value: 25.2 J Grade Count:6 | |
| Coefficient of Friction | 0.260 - 0.550 | 0.260 - 0.550 | Average value: 0.369 Grade Count:6 |
| Tensile Creep Modulus, 1 hour | 1000 - 3400 MPa | 145000 - 493000 psi | Average value: 2410 MPa Grade Count:13 |
| Tensile Creep Modulus, 1000 hours | 450 - 980 MPa | 65300 - 142000 psi | Average value: 706 MPa Grade Count:13 |
| Taber Abrasion, mg/1000 Cycles | 4.00 - 8.00 | 4.00 - 8.00 | Average value: 5.88 Grade Count:8 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+19 ohm-cm | 1.00e+9 - 1.00e+19 ohm-cm | Average value: 7.34e+16 ohm-cm Grade Count:128 |
| Surface Resistance | 1.00e+7 - 2.50e+16 ohm | 1.00e+7 - 2.50e+16 ohm | Average value: 4.47e+14 ohm Grade Count:71 |
| Dielectric Constant | 1.90 - 15.0 | 1.90 - 15.0 | Average value: 4.44 Grade Count:95 |
| Dielectric Strength | 11.8 - 120 kV/mm | 300 - 3050 kV/in | Average value: 35.1 kV/mm Grade Count:98 |
| Dissipation Factor | 0.000200 - 0.320 | 0.000200 - 0.320 | Average value: 0.0682 Grade Count:49 |
| Dielectric Loss Index | 0.0250 - 0.200 | 0.0250 - 0.200 | Average value: 0.107 Grade Count:10 |
| Arc Resistance | 110 - 240 sec | 110 - 240 sec | Average value: 149 sec Grade Count:15 |
| Comparative Tracking Index | 475 - 600 V | 475 - 600 V | Average value: 593 V Grade Count:81 |
| Hot Wire Ignition, HWI | 7.00 - 60.0 sec | 7.00 - 60.0 sec | Average value: 25.9 sec Grade Count:5 |
| High Amp Arc Ignition, HAI | 120 arcs | 120 arcs | Average value: 120 arcs Grade Count:5 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 - 50.0 mm/min | 0.000 - 1.97 in/min | Average value: 11.5 mm/min Grade Count:5 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.700 - 130 µm/m-°C | 0.389 - 72.2 µin/in-°F | Average value: 72.2 µm/m-°C Grade Count:86 |
| CTE, linear, Transverse to Flow | 10.0 - 142 µm/m-°C | 5.56 - 78.9 µin/in-°F | Average value: 86.3 µm/m-°C Grade Count:26 |
| Specific Heat Capacity | 1.67 - 1.70 J/g-°C | 0.399 - 0.406 BTU/lb-°F | Average value: 1.69 J/g-°C Grade Count:17 |
| Thermal Conductivity | 0.200 - 0.330 W/m-K | 1.39 - 2.29 BTU-in/hr-ft²-°F | Average value: 0.274 W/m-K Grade Count:32 |
| Melting Point | 197 - 265 °C | 387 - 509 °F | Average value: 258 °C Grade Count:206 |
| Maximum Service Temperature, Air | 70.0 - 220 °C | 158 - 428 °F | Average value: 136 °C Grade Count:35 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 - 260 °C | 140 - 500 °F | Average value: 213 °C Grade Count:163 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 - 250 °C | 100 - 482 °F | Average value: 81.0 °C Grade Count:227 |
| Deflection Temperature at 8.0 MPa | 50.0 - 60.0 °C | 122 - 140 °F | Average value: 53.0 °C Grade Count:6 |
| Vicat Softening Point | 148 - 255 °C | 298 - 491 °F | Average value: 229 °C Grade Count:43 |
| Minimum Service Temperature, Air | -40.0 - -30.0 °C | -40.0 - -22.0 °F | Average value: -31.7 °C Grade Count:6 |
| Decomposition Temperature | 300 - 310 °C | 572 - 590 °F | Average value: 308 °C Grade Count:10 |
| UL RTI, Electrical | 65.0 - 130 °C | 149 - 266 °F | Average value: 114 °C Grade Count:6 |
| UL RTI, Mechanical with Impact | 65.0 - 75.0 °C | 149 - 167 °F | Average value: 72.5 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 65.0 - 85.0 °C | 149 - 185 °F | Average value: 80.0 °C Grade Count:6 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:121 |
| Oxygen Index | 20.0 - 30.0 % | 20.0 - 30.0 % | Average value: 25.5 % Grade Count:23 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 799 °C Grade Count:14 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 310 °C | 176 - 590 °F | Average value: 207 °C Grade Count:22 |
| Nozzle Temperature | 250 - 293 °C | 482 - 560 °F | Average value: 275 °C Grade Count:15 |
| Melt Temperature | 230 - 310 °C | 446 - 590 °F | Average value: 281 °C Grade Count:91 |
| Mold Temperature | 15.0 - 107 °C | 59.0 - 225 °F | Average value: 69.6 °C Grade Count:96 |
| Drying Temperature | 60.0 - 140 °C | 140 - 284 °F | Average value: 80.6 °C Grade Count:61 |
| Dry Time | 1.00 - 6.00 hour | 1.00 - 6.00 hour | Average value: 3.35 hour Grade Count:56 |
| 2.00 - 6.00 hour @Temperature 80.0 - 80.0 °C | 2.00 - 6.00 hour @Temperature 176 - 176 °F | Average value: 4.00 hour Grade Count:1 | |
| Moisture Content | 0.0200 - 2.50 % | 0.0200 - 2.50 % | Average value: 0.193 % Grade Count:47 |
| Injection Pressure | 30.0 - 140 MPa | 4350 - 20300 psi | Average value: 83.8 MPa Grade Count:36 |
| Hold Pressure | 50.0 - 140 MPa | 7250 - 20300 psi | Average value: 91.9 MPa Grade Count:4 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 3.60 MPa Grade Count:38 |
| Clamp Pressure | 29.4 - 68.7 MPa | 4270 - 9960 psi | Average value: 49.0 MPa Grade Count:3 |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | Average value: 0.511 cm Grade Count:4 |
| Screw Speed | 30.0 - 150 rpm | 30.0 - 150 rpm | Average value: 71.2 rpm Grade Count:31 |