- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.89
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.214
- 拉伸强度 [MPa]: 50.0
- 断裂伸长率 [%]: 58.6
- 弯曲强度 [MPa]: 38.0
- 弯曲模量 [MPa]: 2.48
- 硬度: 98.0
- 热变形温度 [℃]: 190.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 - 1.75 g/cc | 0.0322 - 0.0632 lb/in³ | Average value: 1.36 g/cc Grade Count:100 |
| Filler Content | 5.00 - 40.0 % | 5.00 - 40.0 % | Average value: 21.4 % Grade Count:20 |
| Water Absorption | 0.0500 - 5.60 % | 0.0500 - 5.60 % | Average value: 0.942 % Grade Count:42 |
| Moisture Absorption at Equilibrium | 0.250 - 4.40 % | 0.250 - 4.40 % | Average value: 2.13 % Grade Count:14 |
| Viscosity Measurement | 0.560 - 1.66 | 0.560 - 1.66 | Average value: 0.936 Grade Count:6 |
| Linear Mold Shrinkage | 0.00150 - 0.0280 cm/cm | 0.00150 - 0.0280 in/in | Average value: 0.0118 cm/cm Grade Count:92 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00220 - 0.0270 cm/cm | 0.00220 - 0.0270 in/in | Average value: 0.0167 cm/cm Grade Count:17 |
| Linear Mold Shrinkage, Transverse | 0.00630 - 0.0170 cm/cm | 0.00630 - 0.0170 in/in | Average value: 0.0111 cm/cm Grade Count:19 |
| Melt Flow | 1.00 - 3.00 g/10 min | 1.00 - 3.00 g/10 min | Average value: 2.00 g/10 min Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 - 95.0 | 90.0 - 95.0 | Average value: 92.3 Grade Count:3 |
| Hardness, Rockwell R | 98.0 - 122 | 98.0 - 122 | Average value: 118 Grade Count:29 |
| Tensile Strength, Ultimate | 38.0 - 150 MPa | 5510 - 21800 psi | Average value: 78.1 MPa Grade Count:81 |
| 22.0 - 50.0 MPa @Temperature 60.0 - 120 °C | 3190 - 7250 psi @Temperature 140 - 248 °F | Average value: 36.7 MPa Grade Count:2 | |
| Tensile Strength, Yield | 50.0 - 125 MPa | 7250 - 18200 psi | Average value: 85.9 MPa Grade Count:22 |
| Elongation at Break | 0.500 - 20.0 % | 0.500 - 20.0 % | Average value: 4.46 % Grade Count:90 |
| Elongation at Yield | 2.40 - 11.0 % | 2.40 - 11.0 % | Average value: 5.22 % Grade Count:8 |
| Modulus of Elasticity | 1.70 - 10.0 GPa | 247 - 1450 ksi | Average value: 4.70 GPa Grade Count:66 |
| Flexural Yield Strength | 58.6 - 207 MPa | 8500 - 30000 psi | Average value: 129 MPa Grade Count:81 |
| Flexural Modulus | 2.48 - 10.3 GPa | 360 - 1500 ksi | Average value: 4.60 GPa Grade Count:90 |
| 1.05 - 3.05 GPa @Temperature 60.0 - 120 °C | 152 - 442 ksi @Temperature 140 - 248 °F | Average value: 1.76 GPa Grade Count:2 | |
| Compressive Yield Strength | 31.0 - 68.9 MPa | 4500 - 10000 psi | Average value: 49.6 MPa Grade Count:8 |
| Izod Impact, Notched | 0.214 - 0.694 J/cm | 0.400 - 1.30 ft-lb/in | Average value: 0.409 J/cm Grade Count:60 |
| 0.300 - 0.350 J/cm @Temperature -40.0 - -20.0 °C | 0.562 - 0.656 ft-lb/in @Temperature -40.0 - -4.00 °F | Average value: 0.338 J/cm Grade Count:2 | |
| Izod Impact, Unnotched | 1.01 - 6.41 J/cm | 1.90 - 12.0 ft-lb/in | Average value: 3.16 J/cm Grade Count:40 |
| Izod Impact, Notched (ISO) | 1.50 - 8.00 kJ/m² | 0.714 - 3.81 ft-lb/in² | Average value: 4.38 kJ/m² Grade Count:22 |
| 2.00 - 7.00 kJ/m² @Temperature -30.0 - -30.0 °C | 0.952 - 3.33 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 4.67 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 20.0 - 55.0 kJ/m² | 9.52 - 26.2 ft-lb/in² | Average value: 30.9 kJ/m² Grade Count:7 |
| 18.0 - 50.0 kJ/m² @Temperature -30.0 - -30.0 °C | 8.57 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 31.0 kJ/m² Grade Count:3 | |
| Charpy Impact Unnotched | 1.00 - 6.00 J/cm² | 4.76 - 28.6 ft-lb/in² | Average value: 3.53 J/cm² Grade Count:25 |
| 1.00 - 4.50 J/cm² @Temperature -40.0 - -20.0 °C | 4.76 - 21.4 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 2.48 J/cm² Grade Count:12 | |
| Charpy Impact, Notched | 0.200 - 1.80 J/cm² | 0.952 - 8.57 ft-lb/in² | Average value: 0.675 J/cm² Grade Count:22 |
| 0.100 - 0.800 J/cm² @Temperature -30.0 - -20.0 °C | 0.476 - 3.81 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 0.522 J/cm² Grade Count:9 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+17 ohm-cm | 1.00e+12 - 1.00e+17 ohm-cm | Average value: 3.77e+15 ohm-cm Grade Count:59 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 1.69e+14 ohm Grade Count:22 |
| Dielectric Constant | 3.60 - 6.00 | 3.60 - 6.00 | Average value: 4.24 Grade Count:21 |
| Dielectric Strength | 15.0 - 80.0 kV/mm | 380 - 2030 kV/in | Average value: 28.7 kV/mm Grade Count:45 |
| Dissipation Factor | 0.0150 - 0.0180 | 0.0150 - 0.0180 | Average value: 0.0161 Grade Count:9 |
| Dielectric Loss Index | 0.0150 - 0.150 | 0.0150 - 0.150 | Average value: 0.0825 Grade Count:8 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | Average value: 475 V Grade Count:20 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 73.8 µm/m-°C | 11.0 - 41.0 µin/in-°F | Average value: 52.8 µm/m-°C Grade Count:35 |
| CTE, linear, Transverse to Flow | 50.0 - 67.0 µm/m-°C | 27.8 - 37.2 µin/in-°F | Average value: 58.0 µm/m-°C Grade Count:3 |
| Thermal Conductivity | 0.250 - 0.389 W/m-K | 1.74 - 2.70 BTU-in/hr-ft²-°F | Average value: 0.316 W/m-K Grade Count:12 |
| Melting Point | 254 - 265 °C | 489 - 509 °F | Average value: 258 °C Grade Count:40 |
| Maximum Service Temperature, Air | 80.0 - 180 °C | 176 - 356 °F | Average value: 132 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 190 - 260 °C | 374 - 500 °F | Average value: 229 °C Grade Count:51 |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 - 250 °C | 142 - 482 °F | Average value: 159 °C Grade Count:87 |
| Vicat Softening Point | 225 - 250 °C | 437 - 482 °F | Average value: 240 °C Grade Count:22 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:69 |
| Oxygen Index | 26.0 - 33.0 % | 26.0 - 33.0 % | Average value: 28.0 % Grade Count:5 |
| Glow Wire Test | 650 °C | 1200 °F | Average value: 650 °C Grade Count:11 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | Average value: 284 °C Grade Count:25 |
| Feed Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Average value: 73.3 °C Grade Count:3 |
| Nozzle Temperature | 250 - 304 °C | 482 - 580 °F | Average value: 277 °C Grade Count:9 |
| Melt Temperature | 241 - 310 °C | 465 - 590 °F | Average value: 282 °C Grade Count:47 |
| Mold Temperature | 49.0 - 120 °C | 120 - 248 °F | Average value: 84.8 °C Grade Count:68 |
| Drying Temperature | 75.0 - 107 °C | 167 - 225 °F | Average value: 82.9 °C Grade Count:39 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 3.63 hour Grade Count:32 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:1 | |
| Moisture Content | 0.0200 - 1.80 % | 0.0200 - 1.80 % | Average value: 0.207 % Grade Count:29 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:9 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 94.6 MPa Grade Count:45 |
| Back Pressure | 0.172 - 1.72 MPa | 24.9 - 250 psi | Average value: 0.431 MPa Grade Count:7 |
| Screw Speed | 20.0 - 200 rpm | 20.0 - 200 rpm | Average value: 83.1 rpm Grade Count:8 |