- 密度 [g/cm3]: 1.21
- 吸水率 [%]: 0.2
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 131.0
- 断裂伸长率 [%]: 179
- 弯曲强度 [MPa]: 138.0
- 弯曲模量 [MPa]: 6.89
- 硬度: 115.0
- 热变形温度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 - 1.42 g/cc | 0.0437 - 0.0513 lb/in³ | Average value: 1.32 g/cc Grade Count:17 |
| Water Absorption | 0.200 - 1.80 % | 0.200 - 1.80 % | Average value: 0.967 % Grade Count:12 |
| Linear Mold Shrinkage | 0.00100 - 0.00600 cm/cm | 0.00100 - 0.00600 in/in | Average value: 0.00332 cm/cm Grade Count:17 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 115 - 120 | 115 - 120 | Average value: 118 Grade Count:4 |
| Tensile Strength, Ultimate | 138 - 250 MPa | 20000 - 36300 psi | Average value: 193 MPa Grade Count:14 |
| Tensile Strength, Yield | 131 - 165 MPa | 19000 - 24000 psi | Average value: 149 MPa Grade Count:4 |
| Elongation at Break | 2.00 - 5.00 % | 2.00 - 5.00 % | Average value: 3.31 % Grade Count:7 |
| Elongation at Yield | 2.00 - 3.90 % | 2.00 - 3.90 % | Average value: 2.78 % Grade Count:10 |
| Modulus of Elasticity | 6.90 - 20.0 GPa | 1000 - 2900 ksi | Average value: 12.9 GPa Grade Count:12 |
| Flexural Yield Strength | 179 - 375 MPa | 26000 - 54400 psi | Average value: 273 MPa Grade Count:15 |
| Flexural Modulus | 6.89 - 18.0 GPa | 1000 - 2610 ksi | Average value: 10.8 GPa Grade Count:17 |
| Izod Impact, Notched | 0.530 - 1.17 J/cm | 0.993 - 2.19 ft-lb/in | Average value: 0.842 J/cm Grade Count:9 |
| Charpy Impact Unnotched | 4.00 - 6.50 J/cm² | 19.0 - 30.9 ft-lb/in² | Average value: 5.23 J/cm² Grade Count:10 |
| 5.00 - 5.00 J/cm² @Temperature -30.0 - -30.0 °C | 23.8 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 5.00 J/cm² Grade Count:1 | |
| Charpy Impact, Notched | 1.00 - 1.20 J/cm² | 4.76 - 5.71 ft-lb/in² | Average value: 1.07 J/cm² Grade Count:7 |
| 1.00 - 1.00 J/cm² @Temperature -30.0 - -30.0 °C | 4.76 - 4.76 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 1.00 J/cm² Grade Count:1 | |
| Coefficient of Friction | 0.200 - 0.320 | 0.200 - 0.320 | Average value: 0.287 Grade Count:4 |
| Coefficient of Friction, Static | 0.170 - 0.280 | 0.170 - 0.280 | Average value: 0.250 Grade Count:4 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10.0 - 1.00e+8 ohm | 10.0 - 1.00e+8 ohm | Average value: 8.48e+6 ohm Grade Count:13 |
| Insulation Resistance | 100 - 1.00e+8 ohm | 100 - 1.00e+8 ohm | Average value: 1.11e+7 ohm Grade Count:9 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 30.0 µm/m-°C | 11.0 - 16.7 µin/in-°F | Average value: 22.5 µm/m-°C Grade Count:5 |
| Thermal Conductivity | 0.280 - 0.400 W/m-K | 1.94 - 2.78 BTU-in/hr-ft²-°F | Average value: 0.360 W/m-K Grade Count:3 |
| Melting Point | 249 - 275 °C | 480 - 527 °F | Average value: 261 °C Grade Count:3 |
| Maximum Service Temperature, Air | 120 - 160 °C | 248 - 320 °F | Average value: 140 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 - 256 °C | 446 - 493 °F | Average value: 250 °C Grade Count:6 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 - 257 °C | 428 - 495 °F | Average value: 243 °C Grade Count:12 |
| Flammability, UL94 | HB | HB | Grade Count:6 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | Average value: 290 °C Grade Count:11 |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | Average value: 290 °C Grade Count:9 |
| Melt Temperature | 260 - 310 °C | 500 - 590 °F | Average value: 298 °C Grade Count:14 |
| Mold Temperature | 66.0 - 121 °C | 151 - 250 °F | Average value: 100 °C Grade Count:14 |
| Drying Temperature | 75.0 - 107 °C | 167 - 225 °F | Average value: 90.1 °C Grade Count:12 |
| Dry Time | 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:1 |