- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 0.4
- 缺口冲击强度: 0.196
- 拉伸强度 [MPa]: 73.5
- 断裂伸长率 [%]: 80.0
- 弯曲强度 [MPa]: 13.1
- 弯曲模量 [MPa]: 1.80
- 硬度: 115.0
- 热变形温度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 - 1.62 g/cc | 0.0444 - 0.0585 lb/in³ | Average value: 1.40 g/cc Grade Count:44 |
| Filler Content | 25.0 - 32.0 % | 25.0 - 32.0 % | Average value: 29.9 % Grade Count:9 |
| Water Absorption | 0.400 - 5.50 % | 0.400 - 5.50 % | Average value: 1.60 % Grade Count:20 |
| Moisture Absorption at Equilibrium | 0.170 - 2.30 % | 0.170 - 2.30 % | Average value: 1.33 % Grade Count:10 |
| Water Absorption at Saturation | 5.50 - 8.00 % | 5.50 - 8.00 % | Average value: 6.00 % Grade Count:4 |
| Viscosity Measurement | 0.520 - 145 | 0.520 - 145 | Average value: 49.0 Grade Count:3 |
| Linear Mold Shrinkage | 0.00100 - 0.0200 cm/cm | 0.00100 - 0.0200 in/in | Average value: 0.00999 cm/cm Grade Count:40 |
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.0200 cm/cm | 0.00600 - 0.0200 in/in | Average value: 0.0120 cm/cm Grade Count:12 |
| Melt Flow | 1.00 - 9.50 g/10 min | 1.00 - 9.50 g/10 min | Average value: 4.30 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90.0 | 90.0 | Average value: 90.0 Grade Count:3 |
| Hardness, Rockwell R | 115 - 125 | 115 - 125 | Average value: 120 Grade Count:14 |
| Tensile Strength, Ultimate | 13.1 - 165 MPa | 1900 - 24000 psi | Average value: 68.1 MPa Grade Count:31 |
| 10.5 - 86.8 MPa @Temperature -20.0 - 120 °C | 1520 - 12600 psi @Temperature -4.00 - 248 °F | Average value: 37.8 MPa Grade Count:1 | |
| 10.5 - 86.8 MPa @Strain 0.150 - 11.0 % | 1520 - 12600 psi @Strain 0.150 - 11.0 % | Average value: 37.8 MPa Grade Count:1 | |
| Tensile Strength, Yield | 73.5 - 186 MPa | 10700 - 27000 psi | Average value: 106 MPa Grade Count:15 |
| Elongation at Break | 1.00 - 40.0 % | 1.00 - 40.0 % | Average value: 6.79 % Grade Count:36 |
| Elongation at Yield | 2.30 - 16.0 % | 2.30 - 16.0 % | Average value: 5.35 % Grade Count:5 |
| Modulus of Elasticity | 1.90 - 9.31 GPa | 276 - 1350 ksi | Average value: 5.50 GPa Grade Count:20 |
| Flexural Yield Strength | 80.0 - 255 MPa | 11600 - 37000 psi | Average value: 140 MPa Grade Count:29 |
| Flexural Modulus | 1.80 - 9.65 GPa | 261 - 1400 ksi | Average value: 5.10 GPa Grade Count:35 |
| Izod Impact, Notched | 0.196 - 1.10 J/cm | 0.367 - 2.06 ft-lb/in | Average value: 0.542 J/cm Grade Count:24 |
| 0.520 - 0.520 J/cm @Temperature -40.0 - -40.0 °C | 0.974 - 0.974 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.520 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 2.40 - 16.0 J/cm | 4.50 - 30.0 ft-lb/in | Average value: 8.18 J/cm Grade Count:6 |
| Izod Impact, Notched (ISO) | 2.00 - 13.0 kJ/m² | 0.952 - 6.19 ft-lb/in² | Average value: 6.08 kJ/m² Grade Count:10 |
| 1.90 - 14.0 kJ/m² @Temperature -40.0 - -30.0 °C | 0.904 - 6.66 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 5.84 kJ/m² Grade Count:3 | |
| Izod Impact, Unnotched (ISO) | 52.0 - 85.0 kJ/m² @Temperature -40.0 - -30.0 °C | 24.7 - 40.4 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 74.0 kJ/m² Grade Count:2 |
| Charpy Impact Unnotched | 1.80 J/cm² - NB | 8.57 ft-lb/in² - NB | Average value: 6.85 J/cm² Grade Count:16 |
| 1.10 - 8.00 J/cm² @Temperature -40.0 - -20.0 °C | 5.24 - 38.1 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 3.63 J/cm² Grade Count:8 | |
| Charpy Impact, Notched | 0.200 - 1.20 J/cm² | 0.952 - 5.71 ft-lb/in² | Average value: 0.520 J/cm² Grade Count:16 |
| 0.150 - 1.00 J/cm² @Temperature -40.0 - -20.0 °C | 0.714 - 4.76 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 0.439 J/cm² Grade Count:9 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 115 - 1.00e+17 ohm-cm | 115 - 1.00e+17 ohm-cm | Average value: 9.13e+15 ohm-cm Grade Count:19 |
| Surface Resistance | 1.00e+10 - 1.00e+15 ohm | 1.00e+10 - 1.00e+15 ohm | Average value: 2.43e+14 ohm Grade Count:11 |
| Dielectric Constant | 3.40 - 10.0 | 3.40 - 10.0 | Average value: 4.70 Grade Count:9 |
| Dielectric Strength | 15.0 - 85.0 kV/mm | 380 - 2160 kV/in | Average value: 34.0 kV/mm Grade Count:21 |
| Dissipation Factor | 0.0100 - 0.150 | 0.0100 - 0.150 | Average value: 0.0323 Grade Count:4 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 447 V Grade Count:14 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 19.8 - 500 µm/m-°C | 11.0 - 278 µin/in-°F | Average value: 114 µm/m-°C Grade Count:12 |
| Melting Point | 254 - 265 °C | 490 - 509 °F | Average value: 258 °C Grade Count:28 |
| Maximum Service Temperature, Air | 80.0 - 220 °C | 176 - 428 °F | Average value: 136 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 - 261 °C | 293 - 502 °F | Average value: 227 °C Grade Count:26 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 256 °C | 140 - 493 °F | Average value: 154 °C Grade Count:39 |
| Vicat Softening Point | 200 - 265 °C | 392 - 509 °F | Average value: 237 °C Grade Count:13 |
| UL RTI, Electrical | 65.0 - 120 °C | 149 - 248 °F | Average value: 107 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 98.3 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 65.0 - 115 °C | 149 - 239 °F | Average value: 105 °C Grade Count:3 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:31 |
| Oxygen Index | 24.0 - 37.5 % | 24.0 - 37.5 % | Average value: 28.5 % Grade Count:7 |
| Glow Wire Test | 649 - 960 °C | 1200 - 1760 °F | Average value: 829 °C Grade Count:12 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 250 - 295 °C | 482 - 563 °F | Average value: 279 °C Grade Count:5 |
| Melt Temperature | 241 - 310 °C | 465 - 590 °F | Average value: 279 °C Grade Count:22 |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | Average value: 87.9 °C Grade Count:21 |
| Drying Temperature | 79.4 - 100 °C | 175 - 212 °F | Average value: 85.6 °C Grade Count:20 |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Average value: 3.69 hour Grade Count:18 |
| Moisture Content | 0.0500 - 1.90 % | 0.0500 - 1.90 % | Average value: 0.330 % Grade Count:10 |
| Injection Pressure | 34.5 - 138 MPa | 5000 - 20000 psi | Average value: 95.2 MPa Grade Count:7 |
| Back Pressure | 0.345 - 58.8 MPa | 50.0 - 8530 psi | Average value: 29.5 MPa Grade Count:3 |
| Screw Speed | 30.0 - 120 rpm | 30.0 - 120 rpm | Average value: 55.0 rpm Grade Count:3 |